Search Results

A selection of commercially available chromium and chromium-free post phosphate rinses along with a deionized water rinse were evaluated over several zinc and zinc-alloy coated sheet steels. The test specimens were pretreated and electrocoated on-line in an automotive assembly plant. The effect of the rinse treatments on the cosmetic corrosion performance of the substrates, after 5 years of exposure in an outdoor scab corrosion test was determined. After this exposure none of the rinse treatments had performed better than deionized water rinse on zinc and zinc-iron coated sheet. The zinc-nickel coating showed improved scribe creepage when treated with the Cr+6/Cr+3 rinse. Data is provided comparing the concentration of the treatments used vs scribe creepage and chipping corrosion paint loss.

A method is proposed to qualify automotive component designs in the laboratory using multiaxial real time load/strain input data acquired in the field. Fatigue damage analysis methods are used to edit the field data to produce an accelerated test cycle that retains all of the damaging real time load histories present in the original test cycle. Use of this procedure can contribute to a significant reduction in product design/development time.

Fastener failure due to hydrogen embrittlement is of significant concern in the automotive industry. These types of failures occur unexpectedly. They may be very costly to the automotive company and fastener supplier, not only monetarily, but also in terms of customer satisfaction and safety. This paper is an overview of a program which one automotive company initiated to minimize hydrogen embrittlement in fasteners. The objectives of the program were two-fold. One was to obtain a better understanding of the hydrogen embrittlement phenomena as it relates to automotive fastener materials and processes. The second and most important objective, was to eliminate hydrogen embrittlement failures in vehicles. Early program efforts concentrated on a review of fastener applications and corrosion protection systems to optimize coated fasteners for hydrogen embrittlement resistance.

Higher horsepower per liter engines have put more demand on the crankshaft, often requiring the use of forged steel. This paper examines cost reduction opportunities to offset the penalties associated with forged steel, with raw material and machinability being the primary factors evaluated. A cost model for crankshaft processing is utilized in this paper as a design tool to select the lowest cost material grade. This model is supported by fatigue and machinability data for various steel grades. Materials considered are medium carbon, low alloy, and microalloy steels; the effects of sulfur as a machining enhancer is also studied.

A comprehensive selection of automotive sheet steels were exposed in an outdoor scab corrosion test to provide a base-line of cosmetic corrosion performance. Eighteen different coated sheet steels along with CRS as a control were processed using two commercially available zinc phosphate chemistries. The phosphating was done using both immersion and spray phosphate processes in a laboratory and an automotive assembly plant. Scribe creepage results are reported for 5 years outdoor scab exposure. Comparisons of the scribe creepage behavior of CRS, zinc, and zinc alloy coatings and the effect of the phosphate treatment are provided. An estimate of 10 years field performance is made.

Five heats of vanadium-microalloyed steel with carbon contents from 0.29% to 0.40% and sulfur contents from 0.031% to 0.110% were forged into automotive spindles and air cooled. Three of the steels were continuously cast whereas the other two were ingot cast. The forged spindles were subjected to microstructural analysis, mechanical property testing, full component testing and machinability testing. The microstructures of the five steels consisted of pearlite and ferrite which nucleated on prior austenite grain boundaries and predominantly on intragranularly dispersed sulfide inclusions of the resulfurized grades. Ultimate tensile strengths and room temperature Charpy V-notch impact toughness values were relatively insensitive to processing and compositional variations. The room temperature tensile and room-temperature impact properties ranged from 820 MPa to 1000 MPa (120 to 145 ksi) and from 13 Joules to 19 Joules (10 to 14 ft-lbs), respectively, for the various steels.

The paper presents a new method, based on standard laboratory cup tests, for predicting the formability of materials; in the example provided, the forming potentials of four new materials are shown. The properties of stretchability and drawability, which are the principal factors defining a material's forming limits, may be assessed using the Olsen spherical cup test and the Swift flat-bottomed cup test. In the shape analysis procedure described, the minimum amount of deformation needed to fix a desired shape is determined. Then necessary adjustments to tooling for optimum sheet metal usage are made based on calculations from a new type of chart showing stretch forming ratio and draw forming ratio, providing a comparison of the formabilities of a number of materials.