This paper documents the finite element (FE) analysis of a hot stamping process for high strength aluminum sheet. In this process a 7075 blank, heated above its solvus temperature, was simultaneously die quenched and stamped in a room temperature die to form a B-pillar outer reinforcement. Two modeling approaches have been investigated: an isothermal mechanical model and a non-isothermal coupled thermo-mechanical model. The accuracy of each approach was assessed by comparing the predicted strain and thickness distributions to experimental measurements from a formed panel. The coupled thermo-mechanical model provided the most accurate prediction.

This work demonstrates the feasibility of hot stamping a B-pillar outer panel from aluminum alloy 7075. AA7075 is characterized by a high strength to weight ratio with yield strengths comparable to those of DP and TRIP advanced high strength steels. Applications using AA7075 have typically been limited to the aerospace industry due to the high variable cost associated with forming and joining of these materials. A primary key to implementation in the automotive industry is the development of metal forming methods that produce non-compromised stamped parts at automotive manufacturing volumes and costs. This work explores the feasibility of die quenching a hot blank within a cold die as a means of delivering high strength aluminum sheet parts. A die made from kirksite was used to evaluate the hot stamping process for a B-pillar outer. After the forming/quenching operation, the parts were subjected to an artificial aging process to regain the properties of the T6-temper.

The aluminum alloy 7075-T6 has the potential to be used for structural automotive body components as an alternative to boron steel. Although this alloy shows poor formability at room temperature, it has been demonstrated that hot stamping is a feasible sheet metal process that can be used to overcome the forming issues. Hot stamping is an elevated temperature forming operation in which a hot blank is formed and quenched within a stamping die. Attaining a high quench rate is a critical step of the hot stamping process and corresponds to maximum strength and corrosion resistance. This work looks at measuring the quench rate of AA7075-T6 by way of three different approaches: water, a water-cooled plate, and a bead die. The water-cooled plate and the bead die are laboratory-scale experimental setups designed to replicate the hot stamping/die quenching process.