Failure loads of spot welds are investigated under static and impact loading conditions. A test fixture was designed and used to obtain maximum loads of spot welds under a range of combined opening and shear loads with different loading rates. Optical micrographs of the cross sections of spot welds before and after failure were obtained to understand the failure processes under various loading rates and different combinations of loads. The experimental results indicate that under nearly pure opening loads, the failure occurs along the nugget circumferential boundary. Under combined opening and shear loading conditions, the failure starts from the tensile side of the base metal near the nugget in a necking/shear failure mode. The effects of sheet thickness and combined load on the load carrying behavior of spot welds are investigated under static and impact loading conditions based on the experimental results.

Failure behavior of spot welds is investigated under impact loading conditions. Three different impact speeds were selected to test both HSLA steel and mild steel specimens under combined opening and shear loading conditions. A test fixture was designed and used to obtain the failure loads of spot weld specimens of different thicknesses under a range of combined opening and shear loads with different impact speeds. Accelerometers were installed on the fixtures and the specimens for investigation of the inertia effects. Optical micrographs of the cross sections of failed spot welds were obtained to understand the failure processes in both HSLA steel and mild steel specimens under different combined impact loads. The experimental results indicate that the failure mechanisms of spot welds are very similar for both HSLA steel and mild steel specimens with the same sheet thickness. These micrographs show that the sheet thickness can affect the failure mechanisms.

In this investigation, spot friction welds in aluminum 6111-T4 lap-shear specimens were tested under both quasi-static and dynamic loading conditions. Micrographs of the spot friction welds after testing were examined to understand the failure modes of spot friction welds in lap-shear specimens under different loading conditions. The micrographs indicate that the spot friction welds produced by this particular set of welding parameters failed in interfacial failure mode under both quasi-static and dynamic loading conditions. The load and displacement histories for lap-shear specimens were obtained under quasi-static and dynamic loading conditions at three different impact velocities. The failure loads of spot friction welds in lap-shear specimens under dynamic loading conditions are about 7% larger than those under quasi-static loading conditions.