This newly developed helical spring can be used at a stress level up to 1300 MPa. The material is composed of Fe-C-Si-Mn-Ni-Cr-Mo-V alloy. Its strength-toughness balance was greatly superior to that of other spring steels. To improve the fatigue strength at a higher stress level, decarburization at the surface upon austenitizing was severely controlled, applying induction heating. Then, a special shot peening process, introduced for the first time, was applied to obtain a surface residual stress at the surface of over 1000 MPa. The spring was first applied to a 1992 TOYOTA model car. Plans are to increase the use since the spring material achieves a weight reduction of at least 30 % and, possibly, 35 to 40 %.

We have developed a new torsional damper spring which lowers the torsional rigidity of the clutch disc while retaining its conventional size. The following two items have been adopted in the newly developed spring: 1) A new steel wire which suppresses any core-softening of the element wire through nitriding. 2) A dual-stage shot peening method which uses harder steel shots (rather than conventional shots) in order to obtain an optimal residual stress profile. As a result of evaluating the fatigue characteristics of this spring, it was discovered that its fatigue strength is approximately 35% higher than that of the conventional spring. A clutch disc using this spring was able to absorb rattling noises which conventional clutch discs could not.