Search Results

Alkali and alkaline earth metal impurities found in diesel fuels are potential poisons for diesel exhaust catalysts. Using an accelerated aging procedure, a set of production exhaust systems from a 2011 Ford F250 equipped with a 6.7L diesel engine have been aged to an equivalent of 150,000 miles of thermal aging and metal exposure. These exhaust systems included a diesel oxidation catalyst (DOC), selective catalytic reduction (SCR) catalyst, and diesel particulate filter (DPF). Four separate exhaust systems were aged, each with a different fuel: ULSD containing no measureable metals, B20 containing sodium, B20 containing potassium and B20 containing calcium. Metals levels were selected to simulate the maximum allowable levels in B100 according to the ASTM D6751 standard. Analysis of the aged catalysts included Federal Test Procedure emissions testing with the systems installed on a Ford F250 pickup, bench flow reactor testing of catalyst cores, and electron probe microanalysis (EPMA).

Engine and flow reactor experiments were conducted to determine the impact of biodiesel relative to ultra-low-sulfur diesel (ULSD) on inhibition of the selective catalytic reduction (SCR) reaction over an Fe-zeolite catalyst. Fe-zeolite SCR catalysts have the ability to adsorb and store unburned hydrocarbons (HC) at temperatures below 300°C. These stored HCs inhibit or block NOx-ammonia reaction sites at low temperatures. Although biodiesel is not a hydrocarbon, similar effects are anticipated for unburned biodiesel and its organic combustion products. Flow reactor experiments indicate that in the absence of exposure to HC or B100, NOx conversion begins at between 100° and 200°C. When exposure to unburned fuel occurs at higher temperatures (250°-400°C), the catalyst is able to adsorb a greater mass of biodiesel than of ULSD. Experiments show that when the catalyst is masked with ULSD, NOx conversion is inhibited until it is heated to 400°C.

Testing to investigate biodiesel's impact on the performance of a zeolite-based selective catalytic reduction (SCR) system was conducted. The tests employed a 2004 compliant Cummins ISB with common rail fuel injection, EGR, and variable geometry turbo. This 5.9L, 300HP engine was retrofitted with a Johnson-Matthey DPF + SCR (SCRT™) system. Testing was conducted over eight steady-state engine operating modes which provided a wide range of exhaust temperature and exhaust chemistry conditions. Fuels tested were a 2007 certification quality ultra-low sulfur diesel (ULSD), as well as a soy derived biodiesel in a B20 blend. B20 produced slightly lower catalyst temperatures and higher NO2:NOx ratios relative to ULSD, but no measureable difference in the overall NOx conversion over the SCR system. The dominant variable influencing SCR performance is the catalyst space velocity, which is unchanged with the use of B20.

Tests of ultra-low sulfur diesel blended with soy-biodiesel at 5% and 20% were conducted using a 2002 model year Cummins ISB engine (with exhaust gas recirculation) that had been retrofitted with a passively regenerated catalyzed diesel particulate filter (DPF). Results show that on average, the DPF balance point temperature (BPT) is 45°C and 112°C lower for B20 blends and neat biodiesel, respectively, than for 2007 certification diesel fuel. Biodiesel causes a measurable increase in regeneration rate at a fixed steady-state condition, even at the 5% blending level. The data show no significant differences in NOx emissions for these fuels at the steady-state regeneration conditions, suggesting that differences in soot reactivity are responsible for the observed differences in BPT and regeneration rate.