Strain rate sensitivity is an important material property in the formability of sheet metal. In this study, strain rate sensitivity is evaluated for several different grades of steel. Strain rate sensitivity varies from 0.01 to 0.022 for the steels tested. It was found that formable steels such as IF and AKDQ steels have both high n-value (strain hardening) and m-value (strain rate sensitivity). Positive strain rate sensitivity results in a significant increase in the yield strength and tensile strength at higher strain rates. The n-value decreases with strain rate for all of the steels. The total elongation decreases slightly with strain rate for the lower strength steels but is constant or even increases slightly with strain rate for high strength steels. For a typical AKDQ steel, the increase in yield strength can be as high as 43% for an increase in strain rate from 0.002 /s to 2.0 /s.

Interface friction between sheet metal and tooling in sheet metal forming is examined in different forming modes using laboratory simulative tests. Stretchability is studied by the limiting dome height test; drawability is investigated by a four inch Swift cup draw test and the coefficient of friction is measured by the draw bead simulator under bending and unbending deformation. The responses of the interface friction in six different coated and uncoated steel sheets are studied using seven different lubricants. It is found that the interface friction between sheet metal and tooling is very sensitive to the forming mode and the type of coating. For the same lubricant and coated material, two different forming modes may produce very different results in interface friction. However, overall good and bad lubricants for all forming modes can be determined for a given coated material using these three tests.