The compatibility of plastic materials used in gasoline storage and dispensing applications was determined for test fuels representing neat gasoline (Fuel C), and blends containing 25% ethanol (CE25a), 16% isobutanol (CiBu16a), and 24% isobutanol (CiBu24a). A solubility analysis was also performed and compared to the volume swell results obtained from the test fuel exposures. The plastic specimens were exposed to each test fuel for16 weeks at 60°C. After measuring the wetted volume and hardness, the specimens were dried for 65 hours at 60°C and then remeasured for volume and hardness. Dynamic mechanical analysis (DMA), which measures the storage modulus as a function of temperature, was also performed on the dried specimens to determine the temperature associated with the onset of the glass-to-rubber transition (Tg). For many of the plastic materials, the solubility analysis was able to predict the relative volume swell for each test fuel.

The compatibility of elastomeric materials used in fuel storage and dispensing applications was determined for test fuels representing neat gasoline and gasoline blends containing 10 and 17 vol.% ethanol, and 16 and 24 vol.% isobutanol. The actual test fuel chemistries were based on the aggressive formulations described in SAE J1681 for oxygenated gasoline. Elastomer specimens of fluorocarbon, fluorosilicone, acrylonitrile rubber (NBR), polyurethane, neoprene, styrene butadiene rubber (SBR) and silicone were exposed to the test fuels for 4 weeks at 60°C. After measuring the wetted volume and hardness, the specimens were dried for 20 hours at 60°C and then remeasured for volume and hardness. Dynamic mechanical analysis (DMA) was also performed to determine the glass transition temperature (Tg). Comparison to the original values showed that all elastomer materials experienced volume expansion and softening when wetted by the test fuels.