Tribological Performance of ZnO-Oil Nanofluids at Elevated Temperatures

The tribological performance of nanofluids consisting of ZnO nanoparticles dispersed with a stabilizer in an API Group III oil was investigated. Recent research suggests that these fluids may reduce friction and wear compared to the base oil when used as a lubricant in metal-on-metal tests. The effects of nanoparticle concentration and test temperature on friction and wear were studied. Tests were run at 50°C and 100°C to investigate the viability of the fluids at elevated temperatures because possible applications include use as engine lubricants. Nanofluids showed friction reduction of up to 5.2% and reduced wear by up to 82.8% versus oil with only stabilizer at the highest ZnO concentration and the lowest temperature. Stabilizer increased wear at every concentration, but did not affect friction significantly. Fluid viscosity was also investigated. At 30°C, significant shear-thinning behavior was observed for the 2% ZnO solution, and a viscosity versus shear rate curve was found.
Journal Article

Scuffing Behavior of 4140 Alloy Steel and Ductile Cast Iron

Scuffing is a failure mechanism which can occur in various engineering components, such as engine cylinder kits, gears and cam/followers. In this research, the scuffing behavior of 4140 steel and ductile iron was investigated and compared through ball-on-disk scuffing tests. A step load of 22.2 N every two minutes was applied with a light mineral oil as lubricant to determine the scuffing load. Both materials were heat treated to various hardness and tests were conducted to compare the scuffing behavior of the materials when the tempered hardness of each material was the same. Ductile iron was found to have a consistently high scuffing resistance before tempering and at tempering temperatures lower than 427°C (HRC ≻45). Above 427°C the scuffing resistance decreases. 4140 steel was found to have low scuffing resistance at low tempering temperatures, but as the tempering temperature increases, the scuffing resistance increased.