Search Results

Diesel burners introduce combustion of diesel fuel to raise exhaust gas temperature to Diesel Oxidization Catalyst (DOC) light-off or Diesel Particulate Filter (DPF) regeneration conditions, thereby eliminating the need of engine measures such as post-injections. Such diesel combustion requirement nevertheless poses challenges to burner development especially in combustion control and risk mitigation of DPF material failure. In particular, burner design must satisfy good soot distribution and heat distribution at DPF front face after meeting minimum requirements of ignition, heat release, and backpressure. In burner development, Computational Fluid Dynamics (CFD) models have been developed based on commercial codes for burner thermal and flow management with capability of predicting comprehensive physical and chemical phenomena including turbulence induced mixing, fuel injection, fuel droplet transport, diesel combustion, radiation, conjugate heat transfer and etc.

Automotive exhaust system experiences vibratory and thermal loads. Bogey test had been the major validation method until recent years when the strain-life approach was adopted to evaluate component's fatigue life. In practice, when using the strain-life model to evaluate a component subjected to elevated temperature, temperature effect on component fatigue life is considered by introducing a temperature scale factor KC that is used to scale up the measured nominal strain, hence the mechanical load. This paper intends to propose a method to estimate KC by designing component bench tests at room temperature and at elevated temperature, respectively. Two major failure modes in the exhaust system are investigated and different temperature effects on the base metal fatigue and on the weld or heat-affected zone are analyzed.

A novel Spatially Optimized Diffusion Alloy (SODA) material has been developed and applied to exhaust systems, which are an aggressive environment subject to high temperatures and loads, as well as excessive corrosion. Traditional stainless steels disperse chromium homogeneously throughout the material, with varying amounts ranging from 10% to 20% dependent upon its grade (e.g. 409, 436, 439, 441, and 304). SODA steels, however, offer layered concentrations of chromium, enabling an increased amount along the outer surface for much needed corrosion resistance and aesthetics. This outer layer, typically about 70μm thick, exceeds 20% of chromium concentration locally, but is less than 3% in bulk, offering selective placement of the chromium to minimize its overall usage. Since this layer is metallurgically bonded, it cannot delaminate or separate from its core, enabling durable protection throughout manufacturing processes and full useful life.

This study presents a probabilistic life (failure) and damage assessment approach for components under general fatigue loadings, including constant amplitude loading, step-stress loading, and variable amplitude loading. The approach consists of two parts: (1) an empirical probabilistic distribution obtained by fitting the fatigue failure data at various stress range levels, and (2) an inverse technique, which transforms the probabilistic life distribution to the probabilistic damage distribution at any applied cycle. With this approach, closed-form solutions of damage as function of the applied cycle can be obtained for constant amplitude loading. Under step-stress and variable amplitude loadings, the damage distribution at any cycle can be calculated based on the accumulative damage model in a cycle-by-cycle manner. For Gaussian-type random loading, a cycle-by-cycle equivalent, but a much simpler closed-form solution can be derived.

Fatigue life assessment is an integral part of the durability and reliability evaluation process of vehicle exhaust components and systems. The probabilistic life assessment approaches, including analytical, experimental, and simulation, CAE implementation in particular, are attracting significant attentions in recent years. In this paper, the state-of-the-art probabilistic life assessment methods for vehicle exhausts under combined thermal and mechanical loadings are reviewed and investigated. The loading cases as experienced by the vehicle exhausts are first categorized into isothermal fatigue, anisothermal fatigue, and high-temperature thermomechanical fatigue (TMF) based on the failure mechanisms. Subsequently, the probabilistic life assessment procedures for each category are delineated, with emphasis on product validation.

Driven by diesel engine emission regulation, more emission aftertretment products have been under development by Tenneco to address the Particular Matter (PM) and NOx reduction needs. The T.R.U.E. (Thermal Regeneration Unit for Exhaust) Clean active thermal management system is one of the examples to reduce PM. The system is designed to increase exhaust temperatures for DPF (Diesel Particulate Filter) regeneration. This product is exposed to high temperature and high oxidation. Therefore, thermal fatigue, creep, oxidation and the interaction become critical mechanism to be considered for its durability. One of the key challenges to validate this product is to find a way of accelerated testing for thermal, creep, and oxidation as well as for vibration. In this paper, accelerated durability test strategy for high temperature device like T.R.U.E Clean is addressed.

The low-NOx standard for heavy duty trucks proposed by the California Air Resources Board represents a significant challenge to the engine and aftertreatment system. In this study, exhaust thermal management requirements were quantified using a combination of engine and aftertreatment modeling. First, a 1-D engine model was used to develop a control strategy capable of increasing the exhaust enthalpy and decreasing the engine-out NOx over the initial portion of the cold FTP cycle. The outputs from this model were then used as inputs to a 1-D model of a representative HD aftertreatment system. Several different passive exhaust thermal management technologies were evaluated with this aftertreatment system model, including insulating the downpipe, close-coupling the aftertreatment system, and reducing the thermal inertia of the DOC and DPF; the last option provides the most benefit to early NOx conversion.

Almost one-third of the fuel energy is wasted through the exhaust of a vehicle. An efficient waste heat recovery (WHR) process will undoubtedly lead to improved fuel efficiency and reduced greenhouse gases (GHG) emission. Currently, there are multiple WHR technologies that are being investigated by various entities in the auto industry. One relatively simple device to extract heat energy from the exhaust is a heat exchanger. Heat exchangers are used in some automotive applications to transfer heat from the hot exhaust gas to the colder coolant fluid to raise the coolant temperature. The warmer coolant fluid can be used for several purposes such as; faster heating of the engine’s lubrication oil and transmission fluids during cold starts, and faster cabin heating, which in turn, can potentially improve the overall engine efficiency and reduce exhaust emissions.

With increasing applications of urea SCR for NOx emission reduction, improving the system performance and durability has become a high priority. A typical urea SCR system includes a urea injector, injector housing, mixer, and appropriate pipe configurations to allow continuous urea injection into the exhaust stream and evaporation of urea solution into gaseous products. Continuous operation at various conditions with high NOx reduction is possible, but one problem that threatens the life and performance of these systems is urea deposit. When urea or its byproducts become deposited on the inner surfaces of the system including walls, mixers, injector housings and substrates it can create concerns of backpressure and material deteriorations. In addition, deposits as a waste of reagents can negatively affect engine operation, emissions performance and DEF economy. Urea deposit behavior is explored in terms of heat transfer, pipe geometry, injector layout and mixing mechanisms.

Strength and fatigue life prediction is very difficult for stamped structural steel parts because the manufacturing process alters the localized material properties. Traditional tensile tests cannot be used to obtain material properties due to size limitations. Because of this, FEA predictions are most often “directional” at best. In this paper an improved prediction methodology is suggested. With a material library developed from standard homogenous test specimens, or even textbook material property tables, localized strength and plastic strain numbers can be inferred from localized hardness tests(1). The new method, using standard ABAQUS static analysis (not commercial fatigue analysis software with many unknowns), is shown to be very accurate. This paper compares the new process FEA strength and fatigue life predictions to laboratory test results using statistical confidence intervals.

Fatigue testing and related fatigue life assessment are essential parts of the design and validation processes of vehicle components and systems. Fatigue bench test is one of the most important testing methods for durability and reliability assessment, and its primary function is to construct design curves based on a certain amount of repeated tests, with which recommendations on product design can be advised. How to increase the accuracy of predictions from test results, the associated life assessment, and to reduce the cost through reducing test sample size is an active and continuous effort. In this paper the current engineering practices on constructing design curves for fatigue test data are reviewed first.

Active regeneration systems for cleaning diesel exhaust can operate at extremely high temperatures up to 1000°C. The extremely high temperatures create a unique challenge for the design of regeneration structural components near their melting temperatures. In this paper, the preparation of the sheet specimens and the test set-up based on induction heating for sheet specimens are first presented. Tensile test data at room temperature, 500, 700, 900 and 1100°C are then presented. The yield strength and tensile strength were observed to decrease with decreasing strain rate in tests conducted at 900 and 1100°C but no strain rate dependence was observed in the elastic properties for tests conducted below 900°C. The stress-life relations for under cyclic loading at 700 and 1100°C with and without hold time are then investigated. The fatigue test data show that the hold time at the maximum stress strongly affects the stress-life relation at high temperatures.

Vehicle exhaust components and systems under fatigue loading often show multiple failure modes, which should be treated, at least theoretically, with rigorous advanced bi-modal and multi-modal statistical theories and approaches. These advanced methods are usually applied to mission-critical engineering applications such as nuclear and aerospace, in which large amounts of test data are often available. In the automotive industry, however, the sample size adopted in the product validation is usually small, thus the bi-modal and multi-modal phenomena cannot be distinguished with certainty.

Fatigue life prediction of elastomer NVH suspension products has become an operating norm for OEMs and suppliers during the product quoting process and subsequent technical reviews. This paper reviews a critical plane analysis based fatigue simulation methodology for a front lower control arm. Filled natural rubber behaviors were measured and defined for the analysis, including: stress-strain, fatigue crack growth, strain crystallization, fatigue threshold and initial crack precursor size. A series of four distinct single and dual axis bench durability tests were derived from OEM block cycle specifications, and run to end-of-life as determined via a stiffness loss criterion. The tested parts were then sectioned in order to compare developed failure modes with predicted locations of crack initiation. In all cases, failure mode was accurately predicted by the simulation, and predicted fatigue life preceded actual end-of-life by not more than a factor of 1.4 in life.

A probabilistic distribution function roughly consists of two parts: the middle part and the tails. The fatigue life distribution at a stress/load level is often described with two-parameter lognormal or Weibull distribution functions, which are more suitable for modeling the mean (middle) behaviors. The domains of the conventional probabilistic distribution functions are often unbounded, either infinite small (0 for the two-parameter Weibull) or infinite large or both. For most materials in low- and medium-cycle fatigue regimes, the domains of fatigue lives are usually bounded, and the inclusion of the bounds in a probabilistic model is often critical in some applications, such as product validation and life management. In this paper, four- and five-parameter Weibull distribution functions for the probabilistic distributions with bounds are developed. Finally, the applications of these new models in fatigue data analysis and damage assessment are provided and discussed.

Corrosion-fatigue (CF) and stress corrosion cracking (SCC) have long been recognized as the major degradation and failure mechanisms of engineering materials under combined mechanical loading and corrosive environments. How to model and characterize these failure phenomena and how to screen, rank, and select materials in corrosion-fatigue and stress corrosion cracking resistance is a significant challenge in the automotive industry and many engineering applications. In this paper, the mathematical structure of a superposition-theory based corrosion-fatigue model is investigated and possible closed-form and approximate solutions are sought. Based on the model and the associated solutions and test results, screening and ranking of the materials in fatigue, corrosion-fatigue are discussed.

Road vibrations cause fatigue failures in vehicle components and systems. Therefore, reliable and accurate damage and life assessment is crucial to the durability and reliability performances of vehicles, especially at early design stages. However, durability and reliability assessment is difficult not only because of the unknown underlying damage mechanisms, such as crack initiation and crack growth, but also due to the large uncertainties introduced by many factors during operation. How to effectively and accurately assess the damage status and quantitatively measure the uncertainties in a damage evolution process is an important but still unsolved task in engineering probabilistic analysis. In this paper, a new procedure is developed to assess the durability and reliability performance, and characterize the uncertainties of damage evolution of components under constant amplitude loadings.

Great efforts have been made to develop the ability to accurately and quickly predict the durability and reliability of vehicles in the early development stage, especially for welded joints, which are usually the weakest locations in a vehicle system. A reliable and validated life assessment method is needed to accurately predict how and where a welded part fails, while iterative testing is expensive and time consuming. Recently, structural stress methods based on nodal force/moment are becoming widely accepted in fatigue life assessment of welded structures. There are several variants of structural stress approaches available and two of the most popular methods being used in automotive industry are the Volvo method and the Verity method. Both methods are available in commercial software and some concepts and procedures related the nodal force/moment have already been included in several engineering codes.

The purpose of this work was to initiate a comparative evaluation of the aqueous corrosion resistance of ferritic stainless steels currently used to fabricate automotive exhaust systems. Both acid condensate and double loop electrochemical potentiokinetic reactivation (DL-EPR) testing using both as-received and heat treated test coupons prepared from Types 409, 409Al, 436 and 439 stainless steel was conducted for this purpose. A truncated version of an in-house acid condensate testing protocol revealed that Type 409Al stainless steel was the most resistant to corrosion of the four ferritic stainless steels examined, whereas Type 409 stainless steel was the least resistance to corrosion.

Life testing or test-to-failure method and binomial testing method are the two most commonly used methods in product validation and reliability demonstration. The two-parameter Weibull distribution function is often used in the life testing and almost exclusively used in the extended time testing, which can be considered as an accelerated testing method by appropriately extending the testing time but with significantly reduced testing samples. However, the fatigue data from a wide variety of sources indicate that the three-parameter Weibull distribution function with a threshold parameter at the left tail is more appropriate for fatigue life data with large sample sizes. The uncertainties introduced from the assumptions about the underlying probabilistic distribution would significantly affect the interpretation of the test data and the assessment of the performance of the accelerated binomial testing methods, therefore, the selection of a probabilistic model is critically important.