Search Results

In this work hemp fibers were chemically treated in order to improve the fiber/matrix interaction in hemp fiber/unsaturated polyester composites prepared by a Resin Transfer Molding (RTM) process. Chemicals used for paper sizing (AKD, ASA, Rosin Acid and SMA) as well as a silane compound and sodium hydroxide were used to modify the fibers' surface. The tensile, flexural and impact properties of the resulting materials were measured. A slight improvement in mechanical properties was observed for the SMA, silane and alkali treated specimens. However close analysis of these tests and of the fracture surface of the samples showed that there was no amelioration of the fiber/matrix adhesion. It was found that predicted tensile strengths using the rule of mixture were very close to the experimental values obtained in this work. Finally the properties of an hybrid glass fiber/hemp fiber composite were found to be very promising

The use of natural fibers for polymer composite materials has increased tremendously in the last few years. This type of reinforcements offers many advantages such as low density, low cost, high specific strength and low environmental impacts. The performance of the natural fiber composites are affected by the fiber loading, the individual mechanical properties of each component (fiber and matrix), and the fiber and matrix adhesion. Concerning the interfacial interaction, natural fibers present a major drawback because of poor compatibility of fibers with most hydrophobic thermoplastic and thermoset matrix. Hemp fiber/acrylic composites were manufactured with sheet molding technique recently. Although mechanical tests give promising results, they exhibit low tensile strength resulting from a poor fiber/matrix adhesion. The moisture resistance property of the sheet molded composites also needs further improvement.

One of the key challenges of the wood polymer composites (WPC) is the inadequate toughness partly due to the incompatibility of the natural fibres and PP matrix. In this work, we performed the surface modification of the natural fibre by either in-situ grafting polymerization of butyl acrylate (PBA) or adsorbing matrix-compatible cationic PBA latex on the fibre surfaces. The results indicated that the mechanical properties of the polypropylene (PP) composites containing the modified fibres, unnotched Izod impact strength in particular, have been improved significantly. The influencing factors and the mechanism of toughening process have also been preliminarily investigated.

Use of natural fiber and / or hybrid thermoplastic composites in the automotive industry can provide the advantages of weight reduction, cost reduction and recyclability, in addition to eco-efficiency and renewability compared to synthetic conventional materials. Besides the mechanical performance of the composites, thermal properties, durability, and recyclability of the natural fiber or hybrid composites are also to be investigated to demonstrate their potential candidacy as structural members in automotive applications. The main objective of this research work was to evaluate thermal properties, creep properties, and recyclability of the natural fiber and natural fiber hybrid composites in comparison with 30-40wt% long glass fiber filled thermoplastic composites. Composites were prepared by melt blending the thermoplastic, fiber and compatibilizer followed by granulation and injection molding of the compound into test specimens.

Eco-efficient and cost effective natural fibre - thermoplastic composites have gained attention to a great extent in the automotive industry. Most of the OEM specifications for automotive interior parts, for example, instrument panels, recommend the composite should have a minimum flexural modulus of 1900 MPa, a notched Impact strength greater than 150 J/m at room temperature and a melt flow index of 5 g/10min and above [1, 2 and 3]. The objective of this work was to develop a high performance hybrid composite by injection molding process of the composites made from natural fibre in combination with glass fibre or calcium carbonate in a thermoplastic matrix to meet the specifications required for automotive interior parts applications. Mechanical properties, such as tensile and flexural strengths and moduli of the composites prepared, were found to be highly promising.

Natural fiber mat (NMT) composites are ecologically and energetically beneficial because of their light-weight at high fibre content. This study demonstrated that the use of loose natural fibre in NMT process could lead to tremendous improvement in the shock absorption properties. It is also concluded that in NMT process fibre length above the critical length of fibre hardly affects the mechanical strength. The process is relatively easy one-step molding technique to provide large dimensions. The process also demonstrated promise in reducing the cost of the composite parts by minimizing/eliminating the use of natural fibre nonwoven mat and replacement of glass fibre.

Energy generation and utilization during friction stir spot welding of Al 6061-T6 and AM50 sheet materials are investigated. The dimensions of the stir zones during plunge testing are largely unchanged when the tool rotational speed increases from 1500 RPM to 3000 RPM (for a plunge rate of 1 mm/s) and when the rate of tool penetration increases from 1 mm/s to 10 mm/s (for a tool rotational speed of 3000 RPM). The energy resulting from tool rotation is also unaffected when higher tool rotational speeds are applied. The rotating pin accounts for around 70% and 66% of the energy generated when 6.3 mm thick Al 6061-T6 and AM50 sheet materials are spot welded without the application of a dwell period. In direct contrast, the contribution made by the tool shoulder increases to around 48% (Al 6061-T6) and to 65% (AM50) when a four second long dwell period is incorporated during spot welding of 6.3 mm thick sheets.

Natural fiber reinforced polymer composites are beginning to find their way into the commercial automotive market. But, inadequate adhesion between hydrophilic natural fibers and hydrophobic matrix materials affects the performance of the resulting composites. In this study the effect of an environmental friendly fungal treatment on the adhesion characteristics of natural fibers is investigated. Firstly, changes in acid-base characteristics of the modified hemp fibers were studied using Inverse Gas Chromatography (IGC). Afterwards, composites were prepared using Resin Transfer Molding (RTM) process and the effect of modification on performance and durability of the composites was investigated.