Search Results

The increased use of zinc coatings on steels has led to a decrease in their weldability. Weld current and time need to be increased in order to achieve sound welds on these materials compared to uncoated steels, and electrode tip life suffers greatly due to rapid alloying and degradation. In this work, typical uncoated Class II electrodes were tested along with a TiC metal matrix composite (MMC) coated electrode. Tests were conducted to study the weldability and process of nugget formation for both electrodes on HDG (hot dipped galvanized) HSLA (high strength low alloys) steels. Current and time ranges were constructed for both types of electrodes by varying either the weld current or weld time while holding all other parameters constant. Analysis of weld microstructures was conducted on cross-sectioned welds using SEM (scanning electron microscopy). Using the coated electrodes reduced weld current and times needed to form MWS (minimum weld size) on the coated steels.

In this study, a finite element software application (SORPAS®) is used to simulate the effect of pulsing on the expected weld thermal cycle during resistance spot welding (RSW). The predicted local cooling rates are used in combination with experimental observation to study the effect pulsing has on the microstructure and mechanical properties of Zn-coated DP600 AHSS (1.2mm thick) spot welds. Experimental observation of the weld microstructure was obtained by metallographic procedures and mechanical properties were determined by tensile shear testing. Microstructural changes in the weld metal and heat affect zone (HAZ) were characterized with respect to process parameters.

TiCP/Ni coating has been deposited onto the electrodes by electro-spark deposition to improve electrode life during resistance welding of Zn-coated steels. However, welding results revealed that molten Zn penetrates into coating through the cracks and then reacts with substrate copper alloy to form brasses. In the present work, laser treatment was performed on the TiCP/Ni coated electrodes to eliminate cracks formed in the as-deposited TiCP/Ni coating. In addition, a multi-electro-spark deposition of Ni, TiCP/Ni and Ni has also been carried out to improve coating quality. On the other hand, a TiB2 coating was also investigated. those coatings were characterized by electro-microscopy, energy-dispersive X-ray analysis, X-ray diffraction and micro-hardness tests. The results showed that cracks within the as-deposited TiCP/Ni coating could be eliminated with the use of laser treatment or a multi-layer deposition process.