A high-quality die-casting technology has been developed for lightweight aluminum frame structures that produces high-strength aluminum parts that are also weldable. This new technology has been used in casting frames for motorcycles and snowmobiles and has enabled improved frame designs with far fewer component parts than was possible before. This die-casting technology also results in a significant reduction in energy consumption during the manufacturing process.

This paper describes an experimental method to predict the rolling contact fatigue life of a crankpin in a market vehicle engine. The fatigue life up to pitting was evaluated by two laboratory tests including a fatigue life measurement using a ball-on-disk test machine and a crankpin durability measurement by an engine bench test. The surface observation after the tests revealed that the surface dent triggers pitting in both tests. The Weibull plot of the percent failure vs. cycle to failure as a function of the contact stress was presented. In order to directly evaluate the effect of the contact stress on the lifetime, the lifetime values measured at L50 are plotted in the diagram showing the contact stress vs. cycle to failure. The obtained relation can predict the lifetime under the controlled condition in which the number of maximum torque points is countable.