This paper presents a numerical analysis of the effect of weld induced residual stress on the fatigue behavior of a T-joint. The thick-section T-joint contained 18 individual weld passes and was subjected to fully-reversed, zero-maximum, and zero-minimum fatigue cycling. The effect of the residual stress was demonstrated by comparing the result with and without residual stress. It was concluded that the local fatigue parameters (mean stress, alternating stress, and stress ratio) at the suspected crack initiation site were changed significantly by the residual stresses when the applied stress were other than fully reversed. In addition, the effect of the stress concentration at the weld was more significant that the effect of the residual stress for the applied fatigue loads levels that were considered. The analysis method presented can be used to assess weldment design and process variables.

Currently the U. S. Department of Defense (DoD) exclusively uses potassium acetate (KAc)-based runway deicing fluids (RDFs) to deice and anti-ice military runways and taxiways. Commercial airports predominantly use KAc, but some also use RDFs composed of KAc plus propylene glycol (PG) or urea plus PG. Conventional RDFs have environmental concerns due to toxicity as well as material compatibility problems such as corrosion of aircraft carbon brake-pad components, cadmium-plated landing gear, and airfield lighting fixtures. Under the Strategic Environmental Research and Development Program (SERDP), Battelle tested a series of patented - bio-based RDFs to address these issues. Tests showed that the Battelle RDFs met the mandatory Aerospace Material Specification (AMS) 1435 requirements. These new RDFs have reduced ecotoxicity compared to currently used RDFs and are compliant with all other environmental requirements.

The cost of electroplating zinc die castings can be reduced by employing microcracked or microporous chromium in place of conventional chromium; the former is more effective in improving corrosion performance while conserving nickel. Exposure data are examined and specifications for nickel and chromium content are presented.

Application of electron microscopy to the study of fractures and fracture mechanisms is reviewed. Static fractures and the fracture of multiphased alloys have been studied, and significant information obtained. Striations on the fracture surface are associated with fatigue crack propagation and are directly related to crack growth rates. Various factors such as strength level, corrosive media, and second-phase particles are known to influence the appearance of the striations under the electron microscope. Since the appearance under the microscope of each type of fracture is quite unique, electron microscopic fractography is also an aid in service failure analyses.