Developing lightweight, stiff and crash-resistant vehicle body structures requires a balance between part geometry and material properties. High strength materials suitable for crash resistance impose geometry limitations on depth of draw, radii and wall angles that reduce geometric efficiency. The introduction of 3rd generation Advanced High Strength Steels (AHSS) can potentially change the relationship between strength and geometry and enable simultaneous improvements in both. This paper will demonstrate applicability of 3rd generation AHSS with higher strength and ductility to replace the 780 MPa Dual Phase steel in a sill reinforcement on the current Jeep Cherokee. The focus will be on formability, beginning with virtual simulation and continuing through a demonstration run on the current production stamping tools and press.

Experimental procedures and results of a benchmark test for springback are reported and a complete suite of obtained data is provided for the validation of forming and springback simulation software. The test is usually referred as the Slit-Ring test where a cylindrical cup is first formed by deep drawing and then a ring is cut from the mid-section of the cup. The opening of the ring upon slitting releases the residual stresses in the formed cup and provides a valuable set of easy-to-measure, easy-to-characterize springback data. The test represents a realistic deep draw stamping operation with stretching and bending deformation, and is highly repeatable in a laboratory environment. In this study, six different automotive materials are evaluated.

Advanced high-strength steels (AHSS) are a class of steels that have a minimum tensile strength of 500 MPa. The advantages of AHSS include superior formability and better crash energy absorption compared with conventional low-strength steels having a minimum tensile strength of 270 MPa. Several steels with a minimum tensile strength of 590 MPa have already found use in current vehicles, and others with minimum tensile strength up to 980 MPa have been qualified for use in future vehicle models. Two 780 MPa steels of interest are 780 DP (Dual Phase) and 780 TRIP (TRansformation Induced Plasticity). In this study, an examination was undertaken to compare the resistance spot-welding behavior of commercially produced 1.6 mm-thick, hot-dipped galvannealed, 780 MPa DP and TRIP steel sheet. Included in the study were evaluations of the weld lobes, weld microhardness, and the shear- and cross-tension strengths of resistance spot welds for the two steels.

Studies in an Angular Stretch Bend Test (ASBT) have demonstrated that the failure location moves from the side wall to punch nose area. This occurs as the R/T ratio decreases below a certain limit and applies to most low carbon steels with the exception of Dual Phase (DP) steels. Such behavior in DP steels indicates that bending effects have a severe impact on the formability of DP materials. Therefore, the traditional criterion using the forming limit curve (FLC) is not suitable to assess the formability at punch radius areas for DP steels due in part to its uniqueness of unconventional microstructures. In this paper, a new failure criterion, ‘Bending-modified’ FLC (BFLC), is proposed by extending the traditional FLC using the “Stretch Bendability Index” (SBI) concept for the stretch bendability assessment.

As vehicle development timelines continue to shorten, it is necessary for the full vehicle NVH engineer to be able to predict performance without actual prototypes. There has been significant advancement in the accuracy of finite element modeling techniques of trimmed bodies; however accuracy is still low in the road noise mid frequency range from 150-400Hz. Also, calculation times for these frequencies are long, with very large results files in some cases. To alleviate these limitations, a Hybrid approach has been used, where a finite element suspension and drive train model is coupled with a test based Frequency Response Function (FRF) model of the trimmed body. The predicted road noise level was compared to actual vehicle tests and exhibited excellent correlation.

Low carbon steels are being replaced by advanced high strength steels (AHSS) due to high demand of the future lighter weight vehicle, while still maintaining good or even better crash performance. However, sidewall curl and springback (section opening) have been found to increase as the strength of the sheet metal increases. Experiments have been conducted on the bending under tension (BUT) test to seek an effective control methodology regarding the applications of the advanced high strength steels (AHSS) in this study. Steels that were studied included a low carbon steel (DQSK), two dual phase steels (DP) and a transformation induced plasticity (TRIP) steel. Two different gauges of each AHSS were also included for a gauge sensitivity study. Different processing variables (four different diameter pins combining with five different back tension forces) were applied to the tests, and the springback angle and sidewall curl were measured for bend and bend-unbend areas of the specimen.

A novel performance classification system has been developed for advanced high-strength steel (AHSS). This system considers intrinsic global and local formability parameters derived from standard uniaxial tension tests and is applicable to all current and future AHSS materials. The overall AHSS performance index (P.I.) is defined herein as the product of the ultimate tensile strength (UTS) and the formability index (F.I.), where F.I. is an intermediate strain value between the true uniform strain and the true fracture strain (TFS). Target P.I. values are defined for First Generation AHSS (GEN1), Improved First Generation AHSS (GEN1+), Third Generation AHSS (GEN3), and AHSS Future. Performance is further distinguished by local, balanced, and global formability characteristics and by relative yield strength (yield-to-tensile ratio). Additionally, the influence of tension test specimen geometry and fracture area measurement method on the TFS value was explored.

This paper describes static and fatigue behavior of resistance spot welds with the stack-up of conventional mild and advanced high strength steels, with and without adhesive, based on a set of lap shear and coach peel coupon tests. The coupons were fabricated following specified spot welding and adhesive schedules. The effects of similar and dissimilar steel grade sheet combinations in the joint configuration have been taken into account. Tensile strength of the steels used for the coupons, both as-received and after baked, and cross-section microstructure photographs are included. The spot weld SN relations between this study and the study by Auto/Steel Partnership are compared and discussed.

The cost of fuel and the desire for fuel efficiency continue to drive automobile manufacturers to invest in and to prioritize vehicle designs and performance. There has long been a fundamental understanding that aerodynamic efficiency (drag) has an effect on this phenomenon. The focus of this paper is to demonstrate how emergent aerodynamic performance calculation tools can be efficiently and effectively utilized for realizing improvements to vehicle performance, thereby enhancing customer satisfaction and societal acceptance. These tools include Computational Fluid Dynamic analysis (CFD) which further includes visualization techniques, shape deformation, DOE, and optimization methods, among others.

A typical forming operation of chassis components (control arms, cross members, etc.) often involves edge stretching and/or hole expansion. As a result, the edge split is a common forming failure mode. To overcome this problem, Japanese and European automakers use stretch flange high strength (SFHS) steel due to its high strength and excellent edge stretch capability. Recently, SFHS steel has gained greater attention in North America and is currently being used for upper and lower control arm applications. This paper includes a discussion on general edge stretch issues in forming operations, including material data that demonstrate the higher stretch limit of SFHS steel as compared to other high strength steels. In a case study, SFHS steel is applied to a control arm and finite element analysis (FEA) is conducted to evaluate forming and structural performance.

Axial drop tower crash tests were carried out on a variety of 70-mm outer-diameter continuous-welded cylindrical steel tubes with several thicknesses (t). Ultimate tensile strength (UTS) ranged from less than 300 MPa for a fully stabilized steel to greater than 800 MPa for the advanced high strength steels (AHSS). In the tests, a 520-kg weight is dropped from a height of 3.3 meters to achieve impact velocities of 6.1 to 6.7 m/s (14 to 15 mph). Load and acceleration data are recorded as a function of time as the tube is crushed axially. The results show that, for a given impact condition, the peak and average crush loads of a steel tube is directly proportional to UTS × t2, while axial crush distance is inversely proportional to UTS × t2. As such, crash deformation can be reduced by substituting higher strength steels of the same thickness, or existing crash deformation can be maintained and weight reduction achieved by substituting higher strength steels with reduced thickness.

To evaluate vehicle crash performance in the early design stages, a reliable fracture model is needed in crash simulations to predict material fracture initiation and propagation. In this paper, a generalized incremental stress state dependent damage model (GISSMO) in LS-DYNA® was calibrated and validated for a 780-MPa third generation advanced high strength steels (AHSS), namely 780 XG3TM steel that combines high strength and ductility. The fracture locus of the 780 XG3TM steel was experimentally characterized under various stress states including uniaxial tension, shear, plane strain and equi-biaxial stretch conditions. A process to calibrate the parameters in the GISSMO model was developed and successfully applied to the 780 XG3TM steel using the fracture test data for these stress states.

Power relays for mounting on printed circuit boards with just half of the case volume compared to low-profile ISO microrelays were tested in repetitious switching load operations. Operation voltage was 14 V and relay temperature was 120 °C. The tests for normally open type relays used lamps (11A) and horns (8A), and those for transfer (changeover) type relays used wiper motors (8.5A, intermittent operation). First failure cycles in each of the 10 relay tests were found to be of sufficiently high value, 2.2 million for lamps, 3.3 million for horns, and 2.4 million for wiper motors. Cycles at cumulative failure rates determined that the durability margins of the relays were acceptable for use.

As we continue to create ever-lighter road vehicles, the challenge of balancing weight reduction and structural performance also continues. One of the key parts this occurs on is the hood, where lighter materials (e.g. aluminum) have been used. However, the aerodynamic loads, such as hood lift, are essentially unchanged and are driven by the front fascia and front grille size and styling shape. This paper outlines a combination CFD/FEA prediction method for hood deflection performance at high speeds, by using the surface pressures as boundary conditions for a FEA linear static deflection analysis. Additionally, custom post-processing methods were developed to enhance flow analysis and understanding. This enabled the modification of existing test methods to further improve accuracy to real world conditions. The application of these analytical methods and their correlation with experimental results are discussed in this paper.

Advanced high strength steels (AHSS), such as dual phase (DP) and transformation induced plasticity (TRIP) steels, have been increasingly used in automotive industry. One of the major advantages of AHSS is the excellent crash energy absorption capability. In this study, crash performances were evaluated for four AHSS including DP980, DP780, TRIP780 (780T), and TRIP590 (590T). Axial crush and bending crush tests were performed to evaluate the material crush performance. High strain rate tension test results for those materials were also presented. FEA analyses with parameter sensitivity studies were conducted including strain rate sensitivity effect, part geometry effects, welding models and forming effects. Good correlations between simulation and experimental data were achieved.

To achieve optimal axial and bending crush performance using dual phase steels for components designed for crash energy absorption and/or intrusion resistance applications, the cross sections of the components need to be optimized. In this study, Altair HyperMorph™ and HyperStudy® optimization software were used in defining the shape design variables and the optimization problem setup, and non-linear finite element code LS-DYNA® software was used in crush simulations. Correlated crash simulation models were utilized and the square cross-section was selected as the baseline. The optimized cross-sections for bending and axial crush performance resulted in significant mass and cost savings, particularly with the application of dual phase steels.

The 7003-T4 alloy has been developed for production of motorcycle frame bodies. The developed material has been applied to the 2001 Goldwing motorcycle recently introduced to the world market. During the material development, a designed experiment was planned by which nine 7003 alloy variants were cast and homogenized. The cast billets were extruded into hollow frame tubes on a production extrusion line and the natural aging response of the material was evaluated. The tendency for recrystallized grains at the surface of the extruded tubes was measured and confirmed to be at an acceptable level for painting. The reversion and recovery of mechanical properties during paint curing was evaluated and curing limits were established for mass production. From the results, parametric equations were derived to describe the relationships between mechanical properties, composition and natural aging time to insure design compliance.

Fracture strain data provide essential information for material selection and serve as an important failure criterion in computer simulations of crash events. Traditionally, the fracture strain was measured by evaluating the thinning at fracture using tools such as a microscope or a point micrometer. In the recent decades, digital image correlation (DIC) has evolved as an advanced optical technique to record full-field strain history of materials during deformation. Using this technique, a complete set of the fracture strains (including major, minor, and thickness strains) can be approximated for the material. However, results directly obtained from the DIC can be dependent on the experiment setup and evaluation parameters, which potentially introduce errors to the reported values.

Digital image correlation (DIC) technique has been proved as a potent tool to determine the forming limit curve (FLC) of sheet metal. One of the major technical challenges using the DIC to generate FLC is to accurately pinpoint the onset of localized necking from the DIC data. In addition to the commonly applied ISO 12004-2 standard, a plethora of other DIC data analysis approaches have been developed and used by various users and researchers. In this study, different approaches, including spatial, temporal and hybrid approaches, have been practiced to determine the limit strains at the onset of localized necking. The formability of a 980GEN3 sheet steel was studied in this work using the Marciniak cup test coupled with a DIC system. The resulting forming limits determined by different approaches were compared. Strengths and limitations of each approach were discussed. In addition, the conventional finger-touch approach was excised using specimens with perceivable localized necks.

Forming Limit Diagrams (FLD) have been widely and successfully used in sheet metal stamping as a failure criterion to detect localized necking, which is the most common failure mechanism for conventional steels during forming. However, recent experience from stamping Dual-Phase steels found that, under certain circumstances such as stretching-bend over a small die radius, the sheet metal fails earlier than that predicted by the FLD based on the initiation of a localized neck. It appears that a different failure mechanism and mode are in effect, commonly referred to as “shear fracture” in the sheet metal stamping community. In this paper, experimental and numerical analysis is used to investigate the shear fracture mechanism. Numerical models are established for a stretch-bend test on DP780 steel with a wide range of bend radii for various failure modes. The occurrences of shear fracture are identified by correlating numerical simulation results with test data.