Due to the high power and energy density and also relative safety, lithium ion batteries are receiving increasing acceptability in industrial applications especially in transportation systems with electric traction such as electric vehicles and hybrid electric vehicles. In this regard, to ensure performance reliability, accurate modeling of calendar life of such batteries is a necessity. In fact, potential failure of Li-ion battery packs remains a barrier to commercialization. Battery pack life is a critical feature to warranty and maintenance planning for hybrid vehicles, and will require adaptive control systems to account for the loss in vehicle range, and loss in battery charge and discharge efficiency. Failure not only results in large replacement costs, but also potential safety concerns such as overheating or short circuiting which may lead to fires.

The benefits of deliberately modulating air-to-fuel ratio over a three-way catalyst are disputed. In this work, engine test cell experiments were carried out to assess the performance of a warmed-up Pd/Rh three-way catalyst. The objectives were threefold: first, to determine the best mode of operation; second, to determine if air-to-fuel ratio modulation enhances robustness to transient air-to-fuel ratio disturbances; third, to determine if the conversion efficiency can be manipulated by controlling the shape of the air-to-fuel ratio oscillation. It was observed that the highest conversion efficiency is obtained using a steady air-to-fuel ratio just rich of stoichiometric; however, this mode of operation lacks robustness with respect to transient disturbances and UEGO sensor errors. Robustness can be improved using an oscillating air-to-fuel ratio, but with a sacrifice in peak conversion efficiency.

Machine learning (ML) plays an ever-increasing role in advanced automotive functionality for driver assistance and autonomous operation; however, its adequacy from the perspective of safety certification remains controversial. In this paper, we analyze the impacts that the use of ML within software has on the ISO 26262 safety lifecycle and ask what could be done to address them. We then provide a set of recommendations on how to adapt the standard to better accommodate ML.

This paper examines the application of damage models in tube bending and subsequent hydroforming of AlMg3.5Mn aluminum alloy tubes. An in-house Gurson-based damage model, incorporated within LS-DYNA, has been used for the simulations. The applied damage model contains several void nucleation and growth parameters that must be determined for each material. A simpler straight tube hydroforming process was considered first to check the damage parameters and predicted ductility. Then the model was applied to a sequence of bending and hydroforming. The damage history from pre-bending was mapped to the hydroforming stage, to allow prediction of the overall ductility. The applied forming parameters in the simulation were based on data extracted during the experimental tests. Finally, the numerical results were compared to the experimental data.

The superior formability and local ductility of the emerging class of third generation of advanced high-strength steels (3rd Gen AHSS) compared to their conventional counterparts of the same strength level offer significant advantages for automotive lightweighting and enhanced crash performance. Nevertheless, studies on the material behavior of 3rd Gen AHSS have been limited and there is some uncertainty surrounding the applicability of developed methodologies for conventional dual-phase (DP) steels to this new class of AHSS. The present paper provides a comprehensive study on the quasi-static and dynamic constitutive behavior, formability characterization and prediction, and the fracture behavior of two commercial 3rd Gen AHSS with an ultimate strength of 1180 MPa that will be contrasted with a conventional DP1180. The hardening response to large strain levels was determined experimentally using tensile and shear tests and then validated with 3-D simulations of tensile tests.

Fatigue crack initiation and propagation models predict the fatigue life of welded "T" specimens tested by the Fatigue Design and Evaluation (FDE) Committee of SAE under constant and variable amplitude load histories. The crack propagation equations stipulated by British Standard BS-7910 have been incorporated in a material memory model for cyclic deformation. The simulations begin with the crack initiation model and show how it is used to account for cyclic mean stress relaxation and the effects of periodic overloads. After the cracks initiate the BS-7910 model is applied to predict the crack advance due to either constant or variable amplitude histories. Simulation results correspond to the experimental results with good accuracy.

1 Crack initiation and propagation test data gathered during tests on Keyhole notched samples is used to evaluate a fatigue life prediction technique. Materials tested include a lower strength ManTen steel and a higher strength Boron steel, RQC-100, both tested with constant and variable amplitude histories. Initiation fatigue life is predicted using the usual method of plasticity correction at the notch followed by a Palmgren-Miner summation of damage with mean stress correction. The emphasis of the study is on simulating the crack propagation results. For that phase discretetize da/dN vs ΔK lines and thresholds for negative R ratios, are used specifically to help predict the propagation for one of the VA histories that had a significant negative mean. The open source crack propagation simulation program applies a material memory model to determine the crack advance on a reversal by reversal basis.

Tessellation methods have been applied to characterize second phase particle fields and the degree of clustering present in AA 5754 and 5182 automotive sheet alloys. A model of damage development within these materials has been developed using a damage percolation approach based on measured particle distributions. The model accepts tessellated particle fields in order to capture the spatial distributions of particles, as well as nearest neighbour and cluster parameter data. The model demonstrates how damage initiates and percolates within particle clusters in a stable fashion for the majority of the deformation history. Macro-cracking leading to final failure occurs as a chain reaction with catastrophic void linkage triggered once linkage beyond three or more clusters of voids takes place.

Using standard tensile testing methods, the material properties of AKDQ and DP600 steels tubes along the axial direction were determined. A novel in-situ optical strain mapping system ARAMIS® was utilized to evaluate the strain distribution during tensile testing along the axial direction. Microstructural and damage characterization was carried out using microscopy and image analysis techniques to compare the damage evolution and formability of both materials. Failure in both steels was observed to occur via a ductile failure mode. AKDQ was found to be the more formable material as it can achieve higher strains, total elongations and thinning prior to failure than the higher strength DP600.

This work outlines the evaluation of static and dynamic dent resistance of medium scale structural assemblies fabricated using AA6111 and AA5754. The assemblies fabricated attempt to mimic common automotive hood designs allowing for a parametric study of the support spacing, sheet thickness and panel curvature. Closure panels of AA6111, of two thicknesses (0.8, and 0.9mm), are bonded to re-usable inner panels fabricated using AA5754 to form the structural assemblies tested. While normal practice would use the same alloy for both the inner and the outer, in the current work, AA5754 was adopted for ease of welding. Numerical simulations were performed using LS DYNA. A comparison of experimental and numerically simulated results is presented. The study attempts to establish an understanding of the relationship between structural support conditions and resulting dent depths for both static and dynamic loading conditions.

Small crack growth from notches under variable amplitude loading requires that crack opening stress be followed on a cycle by cycle basis and taken into account in making fatigue life predictions. The use of constant amplitude fatigue life data that ignores changes in crack opening stress due to high stress overloads in variable amplitude fatigue leads to non-conservative fatigue life predictions. Similarly fatigue life predictions based on small crack growth calculations for cracks growing from flaws in notches are non-conservative when constant amplitude crack growth data are used. These non-conservative predictions have, in both cases, been shown to be due to severe reductions in fatigue crack closure arising from large (overload or underload) cycles in a typical service load history.

Fracture characterization of automotive metals under simple shear deformation is critical for the calibration of advanced fracture models employed in forming and crash simulations. In-plane shear fracture tests of high ductility materials have proved challenging since the sample edge fails first in uniaxial tension before the fracture limit in shear is reached at the center of the gage region. Although through-thickness machining is undesirable, it appears required to promote higher strains within the shear zone. The present study seeks to adapt existing in-plane shear geometries, which have otherwise been successful for many automotive materials, to have a local shear zone with a reduced thickness. It is demonstrated that a novel shear zone with a pocket resembling a “peanut” can promote shear fracture within the shear zone while reducing the risk for edge fracture. An emphasis was placed upon machinability and surface quality for the design of the pocket in the shear zone.

New innovations in the field of advanced high strength steels (AHSS) have led to the development of steels with improved stretch-flangeability known as hot-rolled multi-phase (HR) steels. To understand the performance of HR steels, hole expansion tests were conducted on five prototype HR steels and compared with their commercial dual-phase (DP) steel equivalent. A variety of hole edge conditions were considered to study the influence of the shear-affected-zone (SAZ), the surface roughness at the sheared edge and the shear burr orientation. The microstructure of each material was characterized and discussed in relation to its formability for the different edge conditions. It was observed that the bainitic-ferrite microstructure of the HR steels showed superior formability during sheared edge stretching compared to commercial dual-phase steels.

This study was undertaken to examine the role of tool finish orientation on the drawing of zinc-coated steel sheets. Beads of average roughnesses of 0.1 μm and 0.2 μm, finished parallel to and perpendicular to sliding, were used in the drawbead test. Lubrication was provided by unblended base oils of 4.5, 30, and 285 mm2/s @ 40°C, used neat and with a boundary additive, 1% stearic acid. Three types of coated sheet (galvannealed, electrogalvanized, and hot-dip galvanized) were compared to bare AKDQ steel sheet. Results show that lubricant viscosity had the greatest effect on friction, while bead finish orientation and coating type influenced the nature of metal transfer and the galling of the strip. Mixed-film lubrication dominated with the medium and heavy lubricants, here contact area and friction were reduced with increasing lubricant viscosity.

Strict environmental regulations are driving the automotive industry toward electric vehicles as they offer zero emissions. A key component in electric vehicles is the electric motor, where the stator and rotor are manufactured from stacks of thin electrical steel sheets. The electrical steel sheets can be cut in different ways, and the cutting methods may significantly affect the fatigue strength of the component. It is important to understand the effect of the cutting processes on the fatigue properties of electrical steel to ensure there is no premature failure of the electric motor resulting from an improper cutting process. This investigation compared the effect of three different edge preparation methods (stamping, CNC machining, and waterjet cutting) on the fatigue performance of 0.27mm thick electrical steel sheets. To investigate the effect of the edge finish on fatigue behavior, surface roughness was measured for these different samples.

One of the major concerns preventing wider utilization of high strength steels (HSS) and advanced high strength steels (AHSS) in hydroforming is their inherent lower formability, compared to conventional mild steels. The application of the axial forces on the tube ends during a hydroforming operation is often referred to as end-feed, and can facilitate deformation of the tube by postponing failure. This research examines the effect of end-feed on the formability of HSS and AHSS tubes during hydroforming. Through simulation, straight and pre-bent tubes are hydroformed at different levels of end-feed for three materials: DDQ, HSLA350 and DP600.

This research examines the effect of endfeed on the thickness and strains during bending of steel tubes. The tubes were bent using an instrumented rotary draw tube bender and subsequently hydroformed into a diamond-profile outside corner fill die. DQAK tubes with an OD of 76.2 mm and a thickness of 1.55 mm were investigated. Endfeed during bending was found to have a significant effect on the thickness and strains within the tube after bending, and numerical models that were generated showed good agreement with the experimental data. It is shown how slight changes in thickness can cause localized failure during hydroforming, and how excessive die clearances can cause large strains in undesired areas.

Automobile fires are a serious concern to manufacturers and consumers. However, understanding how the fires begin, in the confines of the engine compartment, is a difficult task. One known cause of fires is hot surface ignition (HSI) arising when engine fluids contact hot surfaces in the engine compartment or the exhaust train. In this study, the ignition of automotive gasoline on four hot surfaces: stainless and carbon steels from the heat shields, stainless steel from the exhaust manifold and cast iron cut from an intake manifold, was examined in a well-controlled, model study. Infra-red thermography and thermocouples were used to monitor surface temperatures prior to, during and after the fluid impacted the surface. This allowed evaluation and comparison of temperature evolution during fluid impact and the ignition event, resulting in an improved mechanistic understanding of the fluid/hot surface interaction.

The presence of residual stresses affects the fatigue response of welded components. In the present study of thick welded cantilever specimens, residual stresses were measured in two A36 steel samples, one in the as-welded condition, and one subjected to a short history of bending loads where substantial local plasticity is expected at the fatigue hot-spot weld toe. Extensive X-Ray Diffraction (XRD) measurements describe the residual stress state in a large region above the weld toe both in an untested as-welded sample and in a sample subjected to a short load history that generated an estimated 0.01 strain amplitude at the stress concentration zone at the weld toe. The results show that such a test will significantly alter the welding-induced residual stresses. Fatigue life prediction methods need to be aware that such alterations are possible and incorporate the effects of such cyclic stress relaxation in life computations.

Electrical steels are silicon alloyed steels that possess great magnetic properties, making them the ideal material choice for the stator and rotor cores of electric motors. They are typically comprised of laminated stacks of thin electrical steel sheets. An electric motor can reach high temperatures under a heavy load, and it is important to understand the combined effect of temperature and load on the electrical steel’s performance to ensure the long life and safety of electric vehicles. This study investigated the fatigue strength and failure behavior of a 0.27mm thick electrical steel sheet, where the samples were prepared by a stamping process. Stress-control fatigue tests were performed at both room temperature and 150°C. The S-N curve indicated a decrease in the fatigue strength of the samples at the elevated temperature compared to the room temperature by 15-25 MPa in the LCF and HCF regimes, respectively.