Standard

ABRASION RESISTANCE TESTING—VEHICLE EXTERIOR GRAPHICS AND PIN STRIPING
1989-06-01
HISTORICAL
J1847_198906
This SAE Recommended Practice applies to the abrasion resistance testing of decorative tapes, graphics, and pin striping. It may also have relevance to certain vehicle labels and plastic wood grain film. The resistance to abrasive damage is judged qualitatively by its effect on the legibility, pattern, and color of the graphic marking. This recommended practice is intended as a guide toward standard practice but may be subject to frequent change to keep pace with experience and technical advances. This should be kept in mind when considering the use of this recommended practice.
Standard

ACCELERATED ENVIRONMENTAL TESTING FOR BONDED AUTOMOTIVE ASSEMBLIES
1992-08-01
HISTORICAL
J2100_199208
This SAE Recommended Practice defines conditions to which bonded assemblies can be exposed to simulate environmental aging. These recommendations are generally based on existing Original Equipment Manufacturer requirements at this time. (Environmental specifications used for this proposal were from General Motors, Ford, and Chrysler.) The substrate type, dimension, and number are described by the standard for materials being tested and should include control specimens which receive no environmental aging.
Standard

Abrasion Resistance Testing - Vehicle Exterior Graphics and Pin Striping
2021-01-07
CURRENT
J1847_202101
This SAE Recommended Practice applies to the abrasion resistance testing of decorative tapes, graphics, and pin striping. It may also have relevance to certain vehicle labels and plastic wood grain film. The resistance to abrasive damage is judged qualitatively by its effect on the legibility, pattern, and color of the graphic marking. This recommended practice is intended as a guide toward standard practice but may be subject to frequent change to keep pace with experience and technical advances. This should be kept in mind when considering the use of this recommended practice.
Standard

Accelerated Environmental Testing for Bonded Automotive Assemblies
2021-01-07
CURRENT
J2100_202101
This SAE Recommended Practice defines conditions to which bonded assemblies can be exposed to simulate environmental aging. These recommendations are generally based on existing Original Equipment Manufacturer requirements at this time. (Environmental specifications used for this proposal were from General Motors, Ford, and Chrysler.) The substrate type, dimension, and number are described by the standard for materials being tested and should include control specimens which receive no environmental aging.
Standard

ELASTOMERIC BUSHING "TRAC" APPLICATION CODE
1994-10-01
HISTORICAL
J1883_199410
The bushing "TRAC" code is intended to be a tool that will aid in the definition of the geometric environment for the test, or use, of an elastomeric bushing.
Standard

ELECTRIC HOURMETER SPECIFICATION
1983-03-01
HISTORICAL
J1378_198303
This SAE Recommended Practice establishes minimum requirements for electric hourmeters for general vehicular applications.
Standard

Elastomeric Bushing "TRAC" Application Code
2017-02-09
CURRENT
J1883_201702
The bushing "TRAC" code is intended to be a tool that will aid in the definition of the geometric environment for the test, or use, of an elastomeric bushing.
Standard

GUIDELINES FOR LABORATORY CYCLIC CORROSION TEST PROCEDURES FOR PAINTED AUTOMOTIVE PARTS
1993-10-13
HISTORICAL
J1563_199310
These guidelines are intended for those engineers and scientists who evaluate the corrosion performance of painted automotive parts in laboratory cyclic tests. The guidelines are intended to help ensure that the results of the tests can be used to reach conclusions concerning the variables under study without being confounded by the test procedure itself. The guidelines also serve as a means to assist users of this type of test in obtaining good inter-laboratory agreement of results.
Standard

Guidelines for Laboratory Cyclic Corrosion Test Procedures for Painted Automotive Parts
2016-04-05
CURRENT
J1563_201604
These guidelines are intended for those engineers and scientists who evaluate the corrosion performance of painted automotive parts in laboratory cyclic tests. The guidelines are intended to help ensure that the results of the tests can be used to reach conclusions concerning the variables under study without being confounded by the test procedure itself. The guidelines also serve as a means to assist users of this type of test in obtaining good inter-laboratory agreement of results.
Standard

INDUCTION CURE TEST FOR METAL BONDING ADHESIVES
1987-05-01
HISTORICAL
J1851_198705
This SAE Recommended Practice defines a procedure for determining the adhesion strength characteristics of heat-cured metal bonding adhesives subjected to induction heating.
Standard

Induction Cure Test for Metal Bonding Adhesives
2021-01-07
CURRENT
J1851_202101
This SAE Recommended Practice defines a procedure for determining the adhesion strength characteristics of heat-cured metal bonding adhesives subjected to induction heating.
Standard

Laboratory Corrosion/Fatigue Testing of Vehicle Suspension Coil Springs
2007-06-15
HISTORICAL
J2800_200706
This lab test procedure should be used when evaluating the combined corrosion and fatigue performance for a particular coating system, substrate, process and design. The test is intended to provide an A to B comparison of a proposed coil spring design versus an existing field validated coil spring when subjected to the combined effects of corrosion and fatigue. The corrosion mechanisms covered by this test include general, cosmetic and pitting corrosion. Fatigue testing covers the maximum design stress and/or stress range of the coil spring design (typically defined as excursion from jounce to rebound positions in a vehicle). The effects of gravel and heat are simulated by pre-conditioning the springs prior to fatigue testing. Time dependant corrosion mechanisms such as stress corrosion cracking are not addressed with this test.
Standard

Laboratory Corrosion/Fatigue Testing of Vehicle Suspension Coil Springs
2016-04-01
CURRENT
J2800_201604
This lab test procedure should be used when evaluating the combined corrosion and fatigue performance for a particular coating system, substrate, process and design. The test is intended to provide an A to B comparison of a proposed coil spring design versus an existing field validated coil spring when subjected to the combined effects of corrosion and fatigue. The corrosion mechanisms covered by this test include general, cosmetic and pitting corrosion. Fatigue testing covers the maximum design stress and/or stress range of the coil spring design (typically defined as excursion from jounce to rebound positions in a vehicle). The effects of gravel and heat are simulated by pre-conditioning the springs prior to fatigue testing. Time dependant corrosion mechanisms such as stress corrosion cracking are not addressed with this test.
Standard

Laboratory Cyclic Corrosion Test
2003-12-01
HISTORICAL
J2334_200312
The SAE J2334 lab test procedure should be used when determining corrosion performance for a particular coating system, substrate, process, or design. Since it is a field-correlated test, it can be used as a validation tool as well as a development tool. If corrosion mechanisms other than cosmetic or general corrosion are to be examined using this test, field correlation must be established.
Standard

Laboratory Cyclic Corrosion Test
2016-04-05
CURRENT
J2334_201604
The SAE J2334 lab test procedure should be used when determining corrosion performance for a particular coating system, substrate, process, or design. Since it is a field-correlated test, it can be used as a validation tool as well as a development tool. If corrosion mechanisms other than cosmetic or general corrosion are to be examined using this test, field correlation must be established.
Standard

METHOD OF VISCOSITY TEST FOR AUTOMOTIVE TYPE ADHESIVES, SEALERS, AND DEADENERS
1995-08-01
HISTORICAL
J1524_199508
This SAE Recommended Practice contains a series of test methods for use in measuring the viscosity of automotive-type adhesives, sealers, and deadeners. The test methods which are contained in this document are as follows: 1.1 Brookfield® Method 1.2 Castor-Severs Rheometer or Pressure Flowmeter 1.3 Penetrometer 1.4 Capillary Rheometer 1.5 Plate Rheometers