An advanced low heat rejection engine concept has successfully completed a 100 hour endurance test. The combustion chamber components were insulated with thermal barrier coatings. The engine components included a titanium piston, titanium headface plate, titanium cylinder liner insert, M2 steel valve guides and monolithic zirconia valve seat inserts. The tribological system was composed of a ceramic chrome oxide coated cylinder liner, chrome carbide coated piston rings and an advanced polyolester class lubricant. The top piston compression ring Included a novel design feature to provide self-cleaning of ring groove lubricant deposits to prevent ring face scuffing. The prototype test engine demonstrated 52 percent reduction in radiator heat rejection with reduced intake air aftercooling and strategic forced oil cooling.

Since the early inception of the adiabatic diesel engine in 1974, marked progress has taken place as a result of research efforts performed all over the world. The use of ceramics for heat engines in production applications has been limited to date, but is growing. Ceramic use for production heat engine has included: combustion prechambers, turbochargers, exhaust port liners, top piston ring inserts, glow plugs, oxygen sensors; and additional high temperature friction and wear components. The potential advantages of an adiabatic engine vary greatly with specific application (i.e., commercial vs. military, stationary vs. vehicular, etc.), and thus, a better understanding of the strengths and weaknesses (and associated risks) of advanced adiabatic concepts with respect to materials, tribology, cost, and payoff must be obtained.

The high temperature tribology issue for uncooled Low Heat Rejection (LHR) diesel engines where the cylinder liner piston ring interface exceeds temperatures of 225°C to 250°C has existed for decades. It is a problem that has persistently prohibited advances in non-watercooled LHR engine development. Though the problem is not specific to non-watercooled LHR diesel engines, it is the topic of this research study for the past two and one half years. In the late 1970s and throughout the 1980s, a tremendous amount of research had been placed upon the development of the LHR diesel engine. LHR engine finite element design and cycle simulation models had been generated. Many of these projected the cylinder liner piston ring top ring reversal (TRR) temperature to exceed 540°C[1]. In order for the LHR diesel to succeed, a tribological solution for these high TRR temperatures had to be developed.

An advanced low heat rejection engine concept has been selected based on a trade-off between thermal insulating performance and available technology. The engine concept heat rejection performance is limited by available ring-liner tribology and requires cylinder liner cooling to control the piston top ring reversal temperature. This engine concept is composed of a titanium piston, headface plate and cylinder liner insert with thermal barrier coatings. Monolithic zirconia valve seat inserts, and thermal barrier coated valves and intake-exhaust ports complete the insulation package. The tribological system is composed of chrome oxide coated cylinder, M2 steel top piston ring, M2 steel valve guides, and an advanced polyol ester class lubricant.

Joint development of the adiabatic engine by Cummins Engine Company and the U. S. Army began with a feasibility analysis ten years ago. The effort was initially driven by the expectation of substantial performance improvement, a reduction in cooling system size, and several additional benefits. Program emphasis turned quickly to experimentation with the goal of demonstrating the feasibility of the adiabatic engine in working hardware. Several significant achievements were realized as have been reported earlier. Further development of the adiabatic engine is expected to be more evolutionary, paced by available technology in the areas of materials and tribology. Analysis capability necessary for insulated engine development has been found to be inadequate. Additional effort has gone into the development and validation of insulated engine analysis tools, both for cycle simulation and structural modeling.

Adiabatics, Inc., with the support of the U.S. Army Tank Automotive Research & Development Engineering Center (TARDEC) has developed a low cost, durable ceramic composite cylinder bore coating for diesel engines operating under severe conditions. This bore coating is a ceramic composite consisting primarily of Iron Oxide, Iron Titanate and Partially Stabilized Zirconia. It is applied by unique chemical thermal bonding technology developed at Adiabatics, Inc. and is referred to as Low Temperature Iron Titanate (LTIT). This coating has been tested against a wide range of cylinder bore treatments ranging from hard chrome plate to hard Nickel Silicon Carbide (NikaSil) and found to provide a superior sliding wear surface. It is superior because it is compatible against most common piston ring materials and coatings.

Experimental results focused towards developing tribological surface coatings coupled with liquid lubricant boundary layer effects, for advanced high temperature military diesel engine applications are presented. The primary focus of this work is in the area of advanced, low heat rejection (LHR) high output diesel engines, where high temperature boundary lubrication between the piston ring and the cylinder liner wall surface is critical for successful engine operation. The target temperature focused upon in our research is an operating top ring reversal (TRR) temperature of approximately 538°C. The technology advancement used for this application involves treating porous iron oxide/titanium oxide (Fe2O3/TiO2) and molybdenum (Mo) based composite thermal sprayed coatings with chemical binders to improve coating strength, integrity, and tribological properties. This process dramatically decreases open porosity to form an almost monolithic appearing coating at the surface1.

This paper presents tribological modeling, experimental work, and validation of tribology parameters of a single cylinder turbocharged diesel engine run at various loads, speeds, intake boost pressures, and cylinder liner temperatures. Analysis were made on piston rings and liner materials, rings mechanical and thermal loads, contact pressure between rings and liner, and lubricant conditions. The engine tribology parameters were measured, and used to validate the engine tribology models. These tribology parameters are: oil film thickness, coefficient of friction between rings and liner, friction force, friction power, friction torque, shear rate, shear stress and wear of the sliding surfaces. In order to measure the oil film thickness between rings and liner, a single cylinder AVL turbocharged diesel engine was instrumented to accept the difference in voltage drop method between rings, oil film, and liner.

Thermal barrier coatings (TBC) are perceived as enabling technology to increase low heat rejection (LHR) diesel engine performance and improve its longevity. The state of the art of thermal barrier coating is the plasma spray zirconia. In addition, other material systems have been investigated for the next generation of thermal barrier coatings. The purpose of this TBC program is to focus on developing binder systems with low thermal conductivity materials to improve the coating durability under high load and temperature cyclical conditions encountered in the real engine. Research and development (R&D) and analysis were conducted on aluminum alloy piston for high output turbocharged diesel engine coated with TBC.

The future of maintaining a superior mobile military ground vehicle fleet rests in high power density propulsion systems. As the U.S. Government desires to convert its powerplant base to heavy fuel operation, there arises the opportunity to incorporate new advanced materials into these heavy fuel engines. These newer materials serve the purpose of decreasing powerplant weight and develop new component designs to take advantage of improved strength and temperature capability of those materials. In addition, the military continues the effort for a non-watercooled Low Heat Rejection (LHR) diesel engine. This type of engine demands the use of ceramic and advanced ceramic composite material hardware. Furthermore, today's higher pressure fuel injection systems, coupled with reduced air/fuel ratio as a means of increasing horsepower to size and weight, will require thermal protection or change in material specification for many of the engine's components.

High thermal stresses in the cylinder heads of low heat rejection (LHR) engines can lead to low cycle fatigue failure in the head. In order to decrease these stresses to a more acceptable level, novel designs are introduced. One design utilizes scallops in the bridge area, and three others utilize a high-strength, low thermal conductivity titanium faceplate inserted into the firedeck (combustion face) of a low heat rejection engine cylinder head. The faceplates are 5mm thick disks that span the firedeck from the injector bore to approximately 10mm outside of the cylinder liner. Large-scale finite element models for these four different LHR cylinder head configurations were created, and used to evaluate their strength performance on a pass/fail basis. The complex geometry of this cylinder head required very detailed three-dimensional analysis techniques, especially in the valve bridge area. This area is finely meshed to allow for accurate determination of stress gradients.

Contrary to the thick thermal barrier coating approach used in adiabatic diesel engines, the authors have investigated the merits of thin coatings. Transient heat transfer analysis indicates that the temperature swings experienced at combustion chamber surfaces depend primarily on material thermophysical properties, i.e., conductivity, density, and specific heat. Thus, cyclic temperature swings should be alike whether thick or thin (less than 0.25 mm) coatings are applied, Furthermore, thin coatings would lead to lower mean component temperatures and would be easier to apply than thick coatings. The thinly-coated engine concept offers several advantages including improved volumetric efficiency, lower cylinder liner wall temperatures, improved piston-liner tribological behavior, and improved erosion-corrosion resistance and thus greater component durability.

More stringent regulations have been enforced over the past few years on diesel exhaust emissions. White smoke emission, a characteristic of diesel engines during cold starting, needs to be controlled in order to meet these regulations. This study investigates the sources and constituents of white smoke. The effects of fuel properties, design and operating parameters on the formation and emissions of white smoke are discussed. A new technique is developed to measure the real time gaseous hydrocarbons (HC) as well as the solid and liquid particulates. Experiments were conducted on a single cylinder direct injection diesel engine in a cold room. The gaseous HC emissions are measured using a high frequency response flame ionization detector. The liquid and solid particulates are collected on a paper filter placed upstream of the sampling line of the FID and their masses are determined.