In the past twenty years, the explicit finite element method has been successfully employed for crash simulation. At present, crashworthiness analysis is still basically a calibration based engineering practice, but not a fully predictive process. The increasing expectations and requirements on CAE are even more challenging. To develop a predictive and reliable CAE tool, it is important to investigate the root causes that affect the numerical accuracy and the availability of the analytical method. Some of the challenging issues are discussed here from both theoretical and engineering aspects, such as convergence of explicit finite element method, locking-free shell element, analysis of material rupture, and modeling of spot weld.

Failure behavior of spot welds is investigated under impact loading conditions. Three different impact speeds were selected to test both HSLA steel and mild steel specimens under combined opening and shear loading conditions. A test fixture was designed and used to obtain the failure loads of spot weld specimens of different thicknesses under a range of combined opening and shear loads with different impact speeds. Accelerometers were installed on the fixtures and the specimens for investigation of the inertia effects. Optical micrographs of the cross sections of failed spot welds were obtained to understand the failure processes in both HSLA steel and mild steel specimens under different combined impact loads. The experimental results indicate that the failure mechanisms of spot welds are very similar for both HSLA steel and mild steel specimens with the same sheet thickness. These micrographs show that the sheet thickness can affect the failure mechanisms.

Failure loads of spot welds are investigated under static and impact loading conditions. A test fixture was designed and used to obtain maximum loads of spot welds under a range of combined opening and shear loads with different loading rates. Optical micrographs of the cross sections of spot welds before and after failure were obtained to understand the failure processes under various loading rates and different combinations of loads. The experimental results indicate that under nearly pure opening loads, the failure occurs along the nugget circumferential boundary. Under combined opening and shear loading conditions, the failure starts from the tensile side of the base metal near the nugget in a necking/shear failure mode. The effects of sheet thickness and combined load on the load carrying behavior of spot welds are investigated under static and impact loading conditions based on the experimental results.