Search Results

The compatibility of notable infrastructure elastomers and plastics with DME and its blends with diesel fuel were examined using solubility analysis. The elastomer materials were fluorocarbon, acrylonitrile butadiene rubber (NBR), styrene butadiene (SBR), neoprene, polyurethane and silicone. Plastic materials included polyphenylene sulfide (PPS), polyethylene terephthalate (PET), polytetrafluoroethylene (PTFE), polyvinylidene fluoride (PVDF), polyoxymethylene (POM), polybutylene terephthalate (PBT), polypropylene (PP), high density polyethylene (HDPE), along with several nylon grades and thermosetting resins. These materials have been rigorously studied with other fuel types, and their volume change results were found to correspond well with their predicted solubility levels. A Hansen solubility analysis was performed for each material with DME, diesel, and blends of both fuel components.

The compatibility of elastomer materials used in fuel storage and dispensing applications was determined for an off-highway diesel fuel and a blend containing 20% bio-oil (Bio20) derived from a fast pyrolysis process. (This fuel blend is not to be confused with B20, which is a blend of diesel fuel with 20% biodiesel.) The elastomer types evaluated in this study included fluorocarbon, fluorosilicone, acrylonitrile rubber (NBR), styrene butadiene rubber (SBR), polyurethane, neoprene, and silicone. All of these elastomer types are used in sealing applications, but some, like the nitrile rubbers are also common hose materials. The elastomer specimens were exposed to the two fuel types for 4 weeks at 60°C. After measuring the wetted volume and hardness, the specimens were dried for 65 hours at 60°C and then remeasured. A solubility analysis was performed to better understand the performance of plastic materials in fuel blends composed of bio-oil and diesel.

The compatibility of plastic materials used in fuel storage and dispensing applications was determined for an off-highway diesel fuel and a blend containing 20% bio-oil (Bio20) derived from a fast pyrolysis process. Bio20 is not to be confused with B20, which is a diesel blend containing 20% biodiesel. The feedstock, processing, and chemistry of biodiesel are markedly different from bio-oil. Plastic materials included those identified for use as seals, coatings, piping and fiberglass resins, but many are also used in vehicle fueling systems. The plastic specimens were exposed to the two fuel types for 16 weeks at 60°C. After measuring the wetted volume and hardness, the specimens were dried for 65 hours at 60°C and then remeasured to determine extent of property change. A solubility analysis was performed to better understand the performance of plastic materials in fuel blends composed of bio-oil and diesel.

A high-resolution corrosion probe was placed within the airhorn section of the exhaust gas recirculation (EGR) loop of a heavy-duty diesel engine. The corrosion rate of the mild-steel probe elements was evaluated as a function of fuel sulfur level, EGR fraction, dewpoint margin, and humidity. No significant corrosion was observed while running the engine using a No. 2 grade, < 15ppm sulfur diesel fuel; however, high corrosion rates were observed with No. 2 diesel fuel (∼350 ppm sulfur) while condensing water in the EGR loop. The rate of corrosion on the mild steel elements increased with increasing levels of sulfate in the condensate. However, the engine conditions influencing the sulfate level were not clearly identified in this study.