This specification covers a precipitation hardenable, corrosion- and heat-resistant nickel alloy in the form of seamless tubing 0.125 inch (3.18 mm) and over in nominal OD and 0.015 inch (0.38 mm) and over in nominal wall thickness.
This document covers the recommended practice for determining the acceptability of the dendrite arm spacing (DAS) of D357-T6 aluminum alloy castings required to have tensile strength not lower than 50 ksi (345 MPa).
This document defines a recommended practice for addressing metal additive manufacturing (AM) machine requalification for all fusion-based metal AM machines. In general, this applies to powder bed fusion (PBF) and wire- or powder-fed directed energy deposition (DED) technologies. Plasma, electron beam, or lasers are applicable energy source(s).
This document covers all metal, self-locking wrenching nuts, plate nuts, shank nuts, and gang channel nuts made from a corrosion and heat resistant steel of the type identified under the Unified Numbering System as UNS S66286 and of 160 ksi tensile strength at room temperature, with maximum test temperature of parts at 1200 °F.
This procurement specification covers aircraft quality self-locking nuts for wrenching (hex, spline) and anchor (plate, gang channel, shank) types of nuts made from a corrosion and heat-resistant nickel-base alloy of the type identified under the Unified Numbering System as UNS N07001. Tension height nuts having overall length of threaded portion not less than 1.2 times the nominal thread diameter have 1210 MPa minimum tensile strength at room temperature. Shear height nuts having shorter threaded portion have 1100 MPa minimum tensile strength at room temperature. Maximum test temperature of parts is 730 °C.
This specification covers a magnesium alloy in the form of sheet and plate from 0.016 to 3.000 inches (0.41 to 76.20 mm), inclusive, in thickness (see 8.5).
This specification covers a magnesium alloy in the form of extruded bars, rods, wire, tubing, and profiles up to 40 square inches (258 cm2) in cross-sectional area (solids) and up to 8.5 inches (216 mm) OD by 1.188 inches (30.18 mm) wall thickness (tubing) (see 8.5).
This SAE Aerospace Standard (AS) establishes the minimum requirements for ground-based aircraft deicing/anti-icing methods and procedures to ensure the safe operation of aircraft during icing conditions on the ground. This document does not specify the requirements for particular aircraft models.NOTE: Refer to particular aircraft operator or aircraft manufacturer’s published manuals and procedures.The application of the procedures specified in this document are intended to effectively remove and/or prevent the accumulation of frost, snow, slush, or ice contamination which can seriously affect the aerodynamic performance and/or the controllability of an aircraft. The principal method of treatment employed is the use of fluids qualified to AMS1424 (Type I fluid) and AMS1428 (Type II, III, and IV fluids).All guidelines referred to herein are applicable only in conjunction with the applicable documents.
This specification covers an aluminum alloy in the form of alclad sheet over 0.039 to 0.126 inches (0.99 to 3.20 mm), inclusive, in nominal thickness with a fine-grain core of ASTM No. 6 or finer (see 8.5).
This specification covers an aluminum alloy in the form of extruded rods, bars, and profiles (shapes) 0.040 to 1.500 inches (1.02 to 38.10 mm), inclusive, in thickness, and produced with maximum cross-sectional area of 23.25 square inches (15000 mm2) and a maximum circumscribing circle diameter (circle size) of 15.5 inches (394 mm) (see 2.4.1 and 8.6).
This specification covers an aluminum alloy in the form of sheet and plate 0.017 to 2.000 inches (0.43 to 50.80 mm), inclusive, in nominal thickness (see 8.6).