Gray cast iron brake rotor experiences substantial wear during braking and contributes largely to the wear debris emissions. Surface coating on the gray cast iron rotor represents a trending approach dealing with the problems. In this research, a new plasma electrolytic aluminating (PEA) process was used for preparing an alumina-based ceramic coating with metallurgical bonding to the gray cast iron. Three different types of brake pads (ceramic, semi-metallic and non asbestos organic (NAO)) were used for tribotests. Performances of PEA coatings vs. different brake pad materials were comparatively investigated with respect to their coefficients of friction (COFs) and wear. The PEA-coated brake rotor has a dimple-like surface which promotes the formation of a thin transferred film to protect the rotor from wear. The transferred film materials come from the wear debris of the pads. The secondary plateaus are regenerated on the brake pads through compacting wear debris of the pads.

Ultra-high strength steel (UHSS) and magnesium (Mg) alloy have found their importance in response to automotive strategy of light weighting. UHSS to be metal-formed by hot stamping usually has a hot-dipped aluminum-silicon alloy layer on its surface to prevent the high temperature scaling during the hot stamping and corrosion during applications. In this paper, a plasma electrolytic oxidation (PEO) process was used to produce ceramic oxide coatings on aluminized UHSS and Mg with intention to further improve their corrosion resistances. A potentiodynamic polarization corrosion test was employed to evaluate general corrosion properties of the individual alloys. Galvanic corrosion of the aluminized UHSS and magnesium alloy coupling with and without PEO coatings was studied by a zero resistance ammeter (ZRA) test. It was found that the heating-cooling process simulating the hot stamping would reduce anti-corrosion properties of aluminized UHSS due to the outward iron diffusion.

This research focuses on study of feasibility of using ceramic oxide coatings on the cylinder wall of hypoeutectic aluminum silicon alloy engine blocks. Coatings are achieved in an aqueous electrolytic bath and composed of both alpha and gamma phases of Al2O3 and have shown promising wear resistance. Composition and acidity level of the electrolyte creates a variation of surface roughness, coating hardness and thickness which has direct influence on the wear behavior of the sliding surfaces. The effect of load bearing and coating morphology on coefficient of friction was studied. SEM images of the substrate showed no predominant wear behavior or delamination. Coefficient of friction and wear rate were also measured. This study shows the importance of surface structure on oil retention and wear rate. Coarser coatings can be desirable under starved oil condition since they show lower coefficient of friction.