A unique cascade test facility has been developed for use in the Wichita State University (WSU) water table. Although small in scale, the WSU water table has the advantage of low cost and the ease with which test conditions can be varied. Water table facilities have been used in the past for cascade experiments, especially as analogies for compressible flow visualization of turbine cascades. However, the lack of a quantitative measurement technique at low speeds has precluded the use of the water table as an analogy for testing subsonic compressors and turbines. In the present experiment, the hydrogen bubble flow visualization technique is used to generate bubble time lines, and a CCD (Charge Coupled Device) video camera system captures and digitizes these time line images. A VisualBASIC® computer program is then used to determine the wake velocity profile based on the difference in bubble line positions at successive intervals of time.

An aging aircraft accumulates fatigue cracks commonly referred to as multiple site damage (MSD). A simplified engineering fracture mechanics model, generally referred to as the linkup model (or plastic zone touch model), has been used with some success to describe the MSD fracture phenomenon in 2024-T3 aluminum panels. A disadvantage of the linkup model is that it gives excessively inaccurate results for some configurations. A modified linkup model has been developed through empirical analysis of test data taken from unstiffened panels with MSD cracks at open holes. The modified linkup model was then validated with test data from stiffened panels including single-bay panels with the lead crack centered between stiffeners and two-bay panels with the lead crack centered beneath a severed stiffener. Further validation of the modified linkup model was done with test data from panels with bolted lap joints. Test results were obtained from 112 different panels.

Multiple site damage (MSD) on aging aircraft accumulates from fatigue loading over a period of time. For ductile materials such as 2024-T3 aluminum, MSD may lower the strength below that which is predicted by conventional fracture mechanics. An analytical model referred to as the linkup (or plastic zone touch) model has previously been used to describe this phenomenon. However, the linkup model has been shown to produce inaccurate results for many configurations. This paper describes several modifications of the linkup model developed from empirical analyses. These modified linkup models have been shown to produce accurate results over a wide range of configurations for both unstiffened and stiffened flat 2024-T3 panels with MSD at open holes. These modified models are easy to use and give quick and accurate results over a large range of parameters.