Diesel exhaust systems equipped with selective catalytic reduction (SCR) catalysts based on urea were subjected to an aging process where the exhaust gas temperature was below 300°C. Solid deposits related to urea injection were found on the wall of the exhaust pipe down stream of the urea injector and on a urea mixer in front of the SCR catalyst. In laboratory tests, an aqueous solution of urea (1.5wt%) was dripped onto an SCR catalyst core in a simulated lean gas mixture at a rate corresponding to a 1:1 NH3-to-NOx ratio (NOx = 350ppm) and a space velocity (SV) of 15,000 h-1 at various temperatures. At 300°C and below, urea-related deposits appeared on the SCR catalyst surface and totally plugged the SCR catalyst monolith within 250 hours. When the aging temperature was 350°C or above, no deposits were observed on the SCR catalyst core.