Search Results

Development of reliable magnesium (Mg) to steel joining methods is one of the critical issues in broader applications of Mg in automotive body construction. Ultrasonic spot welding (USW) has been demonstrated successfully to join Mg to steel and to achieve strong joints. In this study, corrosion test of ultrasonic spot welds between 1.6 mm thick Mg AZ31B-H24 and 0.8 mm thick galvanized mild steel, without and with adhesive, was conducted. Adhesive used was a one-component, heat-cured epoxy material, and was applied between overlapped sheets before USW. Corrosion test was conducted with an automotive cyclic corrosion test, which includes cyclic exposures of dipping in the 0.5% sodium chloride (NaCl) bath, a constant humidity environment, and a drying period. Lap shear strength of the joints decreased with the cycles of corrosion exposure. Good joint strengths were retained at the end of 30-cycle test.

A new spot joining technology relying on a consumable joining bit has been developed and evaluated on dual phase (DP) 980 steel and a dissimilar combination of aluminum alloy 5754-O and DP 980. This new process, called friction bit joining (FBJ), uses a consumable bit to create a solid-state joint in sheet materials by the action of cutting and frictional bonding. A series of experiments were done in which different welding parameters were employed and lap shear tension testing was carried out to evaluate performance. The best lap shear values averaged 6.5 kN.

Static and dynamic strength tests were performed on spot welded specimens made of dual-phase (DP) 780 and mild steels (DQSK). Lap-shear (LS) and cross-tension (CT) as well as a new mixed mode specimen were studied using MTS hydraulic universal testing machine for static tests and drop weight tower for dynamic tests. Three weld nugget sizes were made for each steel and CT and LS. DP780 with one weld size was also tested in mixed mode. Load and displacement as functions of time and fracture mode of the spot welds were recorded. Representative data are reported in this paper.

This paper presents on-going finite element modeling efforts of friction stir spot welding (FSSW) process using Abaqus/Explicit as a finite element solver. Three-dimensional coupled thermal-stress model was used to calculate thermo-mechanical response of FSSW process. Adaptive meshing and advection schemes, which makes it possible to maintain mesh quality under large deformations, is utilized to simulate the material flow and temperature distribution in FSSW process. The predicted overall deformation shape of the weld joint resembles that experimentally observed. Temperature and stress graphs in the radial direction as well as temperature-deformation distribution plots are presented.

Ultrasonic spot welding is a novel solid-state joining technique for automotive body structures. The residual stresses, caused by the inhomogeneous deformation during the welding process, are considered to be a major factor affecting the strength and quality of the weld. Many conventional measurement methods cannot be applied because of the small size of the spot weld. In this study, the ISSR/ring-core cutting method is applied to measure the residual stresses on the ultrasonic spot weld. The ISSR possesses the short gage length and high sensitivity. The ring-core cutting was conducted on the back of the spot weld. The tensile residual stresses were obtained. The measured tensile residual stresses added to the operation stresses could cause the initiation of the cracks.

An exploratory study was conducted to investigate the feasibility of friction stir spot welding advanced high-strength steel sheet metals. The fixed pin approach was used to weld 600MPa dual phase steel and 1310MPa martensitic steel. A single tool, made of polycrystalline cubic boron nitride, survived over one hundred welding trials without noticeable degradation and wear. Solid-state metallurgical bonding was produced with welding time in the range of 2 to 3 seconds, although the bonding ligament width was relatively small. The microstructures and hardness variations in the weld regions are discussed. The results from tensile-shear and cross-tensile tests are also presented.

This paper presents on-going finite element modeling efforts of friction stir spot welding (FSSW) process by an explicit finite element code. Adaptive meshing and advection schemes, which makes it possible to maintain mesh quality under large deformations, is utilized to simulate the material flow and temperature distribution in FSSW process. The predicted overall deformation shape of the weld joint resembles that experimentally observed. Temperature and stress graphs in the radial direction as well as temperature-deformation distribution plots are presented. However, refinements of several modeling aspects are needed for more realistic prediction of the FSSW process.

Microstructures and failure mechanisms of spot friction welds (SFW) in aluminum 5754 lap-shear specimens were investigated. In order to study the effect of tool geometry on the joint strength of spot friction welds, a concave tool and a flat tool were used. In order to understand the effect of tool penetration depth on the joint strength, spot friction welds were prepared with two different penetration depths for each tool. The results indicated that the concave tool produced slightly higher joint strength than the flat tool. The joint strength did not change for the two depths for the flat tool whereas the joint strength slightly increases as the penetration depth increases for the concave tool. The experimental results show that the failure mechanism is necking and shearing for the spot friction welds made by both tools. The failure was initiated and fractured through the upper sheet under the shoulder indentation near the crack tip.