With the increasing demand for safety, energy saving and emission reduction, Advanced High Strength Steels (AHSS) have become very attractive materials for automobile makers. Welding of AHSS remains one of the technical challenges in the successful application of AHSS in automobile structures, especially when durability of the welded structures is required. In this study, 2.0 mm uncoated DP780 was investigated. GMAW welding parameters for lap joints of this steel were developed in order to obtain different weld geometries defined by weld toe angle, weld leg sizes, and weld penetration. Metallurgical properties of the joints were evaluated using optical microscopy and scanning electron microscopy (SEM). Static and fatigue tests were conducted on the welded joints. Effect of weld geometry and HAZ softening on fatigue performance including fatigue life, crack initiation site and propagation path of the joints will be analyzed.

In this study, fatigue performance of Gas Metal Arc Welded (GMAW) joint for 1.5 mm uncoated DP780 and 1.0 mm and aluminized coated boron (or USIBOR) steel was investigated. Metallurgical properties of DP780 to coated boron steel dissimilar steel lap joints were evaluated using optical microscopy. Microhardness traverse, static and fatigue tests were conducted on these joints. Finite element analysis (FEA) was used to identify the stress distribution of the weld joints with different stack-ups and at same loading conditions. It was found that position of the material (top or bottom in lap joint configuration) had a significant impact on fatigue performance of the dissimilar joint. The amount of heat introduced by welding to coated boron steel is also believed to be important to the fatigue performance of the dissimilar joints. The findings in this study can be used when aluminized boron steel is involved in dissimilar steel and dissimilar thickness GMAW lap joint design.