A linerless aluminum (Al) engine block has potential to reduce the weight of an automotive engine and improve the fuel economy. However, the Al cylinder surface of an aluminum engine block is not usually strong enough to withstand the sliding wear against piston rings. A few surface processing technologies are used to protect the surface of cylinders. Among them, a thermal spraying coating, such as plasma transferred wire arc (PTWA) is already popular. Plasma electrolytic oxidation (PEO) coating is also proposed for increasing the wear resistance of aluminum-silicon (Al-Si) alloys and reducing the friction between the cylinder and piston. In this work, two different PEO coatings with a thickness of around 23 μm were prepared on an Al-Si alloy A356, and a high speed pin-on-disc tribometer was used to study the tribological behavior of the coatings at oil lubricant conditions. A cast iron sample was also used to do similar tribological tests for comparison.

Friction between the piston and cylinder accounts for large amount of the friction losses in an internal combustion (IC) engine. Therefore, any effort to minimize such a friction will also result in higher efficiency, lower fuel consumption and reduced emissions. Plasma electrolytic oxidation (PEO) coating is considered as a hard ceramic coating which can provide a dimpled surface for oil retention to bear the wear and reduce the friction from sliding piston rings. In this work, a high speed pin-on-disc tribometer was used to generate the boundary, mixed and hydrodynamic lubrication regimes. Five different lubricating oils and two different loads were applied to do the tribotests and the COFs of a PEO coating were studied. The results show that the PEO coating indeed had a lower COF in a lower viscosity lubricating oil, and a smaller load was beneficial to form the mixed and hydrodynamic lubricating regimes earlier.