A failure mode in engine components that undermines engine reliability is scuffing; defined as sudden catastrophic failure of sliding surfaces. Usually accompanied by a rapid rise in friction and temperature, occurrence of scuffing marks the end of the component's useful life. At Argonne National Laboratory, we recently developed low-friction amorphous carbon coatings with exceptional tribological properties. The present study evaluates the scuffing performance of three variations of the carbon coating deposited on H-13 steel surfaces and lubricated with base-stock and fully formulated synthetic Poly-alfa-olefin (PAO) lubricants. Using a ball-on-flat contact configuration in reciprocating sliding, we found that although the coatings reduced friction slightly, they increased scuffing resistance significantly when one of the sliding surfaces was coated when compared to uncoated steel-on-steel contact.

Amorphous carbon coatings with very low friction properties were recently developed at Argonne National Laboratory. These coatings have shown good promise in mitigating excessive wear and scuffing problems associated with low-lubricity diesel fuels. To reduce the negative effect of sulfur and other lubricant additives in poisoning the after-treatment catalyst, a lubricant formulation with a low level of sulfur may be needed. Exclusion of proven sulfur-containing extreme pressure (EP) and antiwear additives from oils will require other measures to ensure durability of critical lubricated components. The low-friction carbon coating has the potential for such applications. In the present study, we evaluated the friction and wear attributes of three variations of the coating under a boundary lubrication regime. Tests were conducted with both synthetic and mineral oil lubricants using a ball-on-flat contact configuration in reciprocating sliding.