Search Results

Since wear is a not a material property, but a tribological system property, it is of great importance to know the wear, friction and lubrication behavior of materials tested in bench equipment. This work presents reciprocating pin-on-plate bench tests results, with gas nitrided stainless steel pins and gray cast iron plates. The testing conditions were 0.5 and 3.2 Hz frequency, 20 and 600N applied load and 100 and 150 °C. Under these conditions, mild to severe wear transition was observed. It was noticed noise emission changes at wear transition. This noise change could be used to verify wear transition mechanism.

The growing use of tribotest has been helping the researches to understand the actuation mechanisms of additives on the friction and wear control of engine parts. But, it is common to observe differences between the tribofilms formed in real situation from that obtained using tribotests. Furthermore, the automakers have difficulty to correlate the results obtained using tribotests with that performed using engines in dynamometers. For the piston ring/cylinder bore tribosystem is almost impossible to reproduce its real tribosystem using tribotests. Therefore simplifications are necessary and they affect the tribochemical behavior of the tribosystem. To understand how these simplifications and the test parameters affect the tribochemical behavior of the simplified tribosystem is critical to design a tribotest that correlate well with the real situation.