The characterization of the thermal and vibration environment of the exhaust systems of three modern day diesel engines, with displacements ranging from 1.9 liter to 12.7 liter, was carried out to support the development of exhaust after treatment components. Tri-axial accelerometer and in pipe thermocouple measurements were recorded at several locations along the exhaust systems during vehicle acceleration and steady driving conditions up to 70 mph. The vehicles were loaded to various gross weight configurations to provide a wide range of engine load conditions. Narrow band and octave band vibration power spectral densities are presented and conclusions are drawn as to the spectral content of the exhaust vibration environment and its distribution along the exhaust system. Temperature time histories during vehicle acceleration runs are likewise presented to indicate expected peak exhaust temperatures.

Mat material durability data in the form of fragility curves were generated in a critical temperature region for three intumescent mat materials considered for low temperature converter applications. The mat materials were tested in a tourniquet wrap converter configuration employing a cylindrical ceramic substrate. Prior to developing durability data for these mat materials, the test items were subjected to various environmental thermal and/or vibration aging conditions. Mat material fragility data were generated in terms of the dynamic force required to impose prescribed differential motion between the can and substrate, thereby, subjecting the mat material to a dynamic shearing like that expected during resonant excitation. As expected, it was found that the mat material capacity to resist shearing deformation decreased when the test samples were subjected to 36 hours of low temperature thermal cyclic aging.

The design of a canned ceramic oval converter, 77mm by 146.8mm, is described along with subsequent demonstration of its high temperature (1050°C) durability. A new mat deterioration phenomenon was recognized, and will be described. The mat deterioration results from sintering of the vermiculite and glass fiber structure when exposed to temperatures greater than approximately 1000°C. Due to the extremely high temperature experienced in the supporting mat of an oval converter exposed to 1050°C, an alternative mat configuration was utilized to eliminate potential mat sintering. An inner layer of non-intumescent mat (1500g/m2) was used in conjunction with an outer layer of intumescent mat (3100g/m2). The inner mat provided sufficient thermal protection to the outer intumescent mat, maintaining considerable holding pressure on the ceramic substrate. A tourniquet closure technique was developed to uniformly compress a hybrid mat system around the entire perimeter of the oval converter.