Search Results

Quantitative in-use pressure measurements were taken from packaging ceramic substrates with the SoftMountSM technology and two more traditional technologies, stuffing and tourniquet. Each technology was assessed using four separate mat materials. Mat selection enhanced the application of the SoftMountSM technology through the reduced pressures applied to the substrate during packaging. High temperature and low temperature thermal cycling studies were performed on the canned converters for the three packaging technologies so that an evaluation could be made of converter durability. The SoftMountSM packaging technology yielded the lowest pressures of all the processes studied, regardless of mat type. The laminar hybrid mat evaluated yielded the best combination of pressure and durability performance. Low temperature residual shear strengths following thermal cycling of the converters showed good correlation between the SoftMountSM technology and the stuffing method.

Mat material durability data in the form of fragility curves were generated in a critical temperature region for three intumescent mat materials considered for low temperature converter applications. The mat materials were tested in a tourniquet wrap converter configuration employing a cylindrical ceramic substrate. Prior to developing durability data for these mat materials, the test items were subjected to various environmental thermal and/or vibration aging conditions. Mat material fragility data were generated in terms of the dynamic force required to impose prescribed differential motion between the can and substrate, thereby, subjecting the mat material to a dynamic shearing like that expected during resonant excitation. As expected, it was found that the mat material capacity to resist shearing deformation decreased when the test samples were subjected to 36 hours of low temperature thermal cyclic aging.

The design of a canned ceramic oval converter, 77mm by 146.8mm, is described along with subsequent demonstration of its high temperature (1050°C) durability. A new mat deterioration phenomenon was recognized, and will be described. The mat deterioration results from sintering of the vermiculite and glass fiber structure when exposed to temperatures greater than approximately 1000°C. Due to the extremely high temperature experienced in the supporting mat of an oval converter exposed to 1050°C, an alternative mat configuration was utilized to eliminate potential mat sintering. An inner layer of non-intumescent mat (1500g/m2) was used in conjunction with an outer layer of intumescent mat (3100g/m2). The inner mat provided sufficient thermal protection to the outer intumescent mat, maintaining considerable holding pressure on the ceramic substrate. A tourniquet closure technique was developed to uniformly compress a hybrid mat system around the entire perimeter of the oval converter.

In this study quantitative techniques were established to assess the low temperature durability of commercially available mat systems. A new low temperature dynamic resistive thermal exposure (LT-RTE) test method was developed. The mats were evaluated in thermal cycling with maximum substrate skin temperatures from 280°C to 450°C. Results indicate that at low use temperatures the residual shear strength of the mat fell to ∼5-15KPa following 280°C cycling. Under the same LT-RTE exposure conditions an equivalent mat system, following thermal preconditioning to 500°C for 3 hours, possessed a residual shear strength of ∼30KPa. An alternative mat system with a lower shot content fiber was also evaluated, following the same thermal preconditioning previously described. This alternative mat was found to exhibit substantially higher residual shear strengths following LT-RTE aging. A residual shear strength of ∼95KPa was observed for this alternative mat following 280°C LT-RTE aging.