This paper presents the progress of an ongoing vehicle micro corrosion environment study. The goal of the study is to develop an improved method for estimating vehicle corrosion based on the Total Vehicle Accelerated Corrosion Test at the Arizona Proving Ground (APG). Although the APG test greatly accelerates vehicle corrosion compared to the field, the “acceleration factor” varies considerably from site-to-site around the vehicle. This method accounts for the difference in corrosivity of various local corrosion environments from site-to-site at APG and in the field. Correlations of vehicle microenvironments with the macroenvironment (weather) and the occurrence of various environmental conditions at microenvironments are essential to the study. A comparison of results from APG versus field measurements generated using a cold rolled steel based corrosion sensor is presented.

Bare magnesium is not compatible with the zinc phosphate process commonly used in automotive manufacturing today. If a magnesium component is assembled onto the vehicle prior to the phosphate process, it must be coated beforehand to prevent magnesium dissolution in the phosphate bath. In addition, for a component that must function in very corrosive environments, galvanic corrosion problems also need to be addressed because the component is most likely to be connected with a more noble metal such as steel fasteners or to another component made of steel or aluminum. In this paper, several coatings were evaluated for their effectiveness in stopping magnesium dissolution during the phosphate process and preventing galvanic corrosion. The results show that a porous anodized coating or a very thin chemical conversion coating does not completely stop magnesium dissolution during the phosphate process.