Technical Paper

Low Friction Property and its Mechanism of DLC-Si Films Under Dry Sliding Conditions

2007-04-16
2007-01-1015
Diamond-like carbon (DLC) films are of significant interest for the automobile field, because they possess the potential to improve friction properties under various sliding conditions. Among the various DLC films, the authors focus on silicon-containing DLC (DLC-Si) films, which exhibit extremely low friction coefficient under dry sliding conditions in an ambient air atmosphere. The aim of this study is to examine the influence of silicon content in DLC-Si films on the friction property of the films, and to clarify the low friction mechanism of the films. The friction test was conducted under dry sliding conditions. It was found that the films have an exceedingly low friction coefficient (about 0.05) ranging in silicon content from 4 at% to 17 at%. In order to examine the low friction mechanism of the films, surface analyses were done on the wear surface of DLC-Si films slid against bearing steel.
Technical Paper

Influence of Engine Oil Viscosity on Piston Ring and Cam Face Wear

1993-10-01
932782
The influence of engine oil viscosity on the wear of piston rings and cam faces has been investigated by fired engine tests using a radioisotope (RI) tracer technique. High-temperature and high-shear-rate (HTHS; 150°C, 1O6 s-1) viscosities of the experimental oils prepared are 2.2, 2.4, 2.6 and 3.1 mPa•s. At an oil temperature of 90°C the wear of piston rings and cam faces did not increase, even if the HTHS viscosity was lowered down to 2.2 mPa•s. However, both piston rings and cam faces exhibited an increase in wear below 2.4 mPa•s at 130°C. It was also recognized that valve train wear did not significantly increase with reducing viscosity in the motored engine tests at a temperature of 50°C. From these test results, it was suggested that the oil with the HTHS viscosity of 2.6 mPa•s sufficiently demonstrates the antiwear performance equivalent to that with around 3.0 mPa•s for application to piston rings and cam faces.
X