Search Results

Base metal/zeolite catalysts, particularly containing copper and iron, are among the leading candidates for treatment of NOx emissions for diesel applications. Even with the use of ultra low sulfur fuel, sulfur poisoning is still a durability issue for base metal/zeolite SCR catalysts. In this study, the impact of sulfur poisoning on SCR activity and the stored sulfur removal effectiveness were investigated on several Cu and Fe/zeolite SCR catalysts after different thermal aging. The impact of sulfur was more significant on the Cu than on Fe/zeolite SCR catalysts for the NOx activity. It was found that the sensitivity of thermal aging status to the sulfur poisoning impact was different. The impact of sulfur on NOx activity changed with thermal aging on some catalysts, while it remained relatively the same for other catalysts. The most thermally durable SCR catalyst was not necessarily the most durable to sulfur poisoning.

Copper/zeolite catalysts are the leading urea SCR catalysts for NOx emission treatment in diesel applications. Sulfur poisoning directly impacts the overall SCR performance and is still a durability issue for Cu/zeolite SCR catalysts. Most studies on sulfur poisoning of Cu/zeolite SCR catalysts have been based on SO2 as the poisoning agent. It is important to investigate the relative poisoning effects of SO3, especially for systems with DOCs in front of Cu/zeolite SCR catalysts. It was observed that SCR activity was significantly reduced for samples poisoned by SO3 vs. those poisoned by SO2. The sulfur was released mainly as SO2 for both samples poisoned by SO2 and SO3. The temperatures and the magnitudes of released SO2 peaks however, were very different between the samples poisoned by SO2 vs. SO3. The results indicate that sulfur poisoning by SO2 and SO3 are not equivalent, with different poisoning mechanisms and impacts.

Promising lean NOx trap (LNT) results on lean-burn gasoline engines have encouraged the development of LNTs for diesel applications. Although the fundamentals of LNT are common for both gasoline and diesel applications, there are major differences due to the character of engine operation and control strategies. The sulfur tolerance and thermal durability of current state-of-the-art diesel LNTs under the conditions that represent the thermal and chemical conditions in diesel exhaust were investigated in a laboratory flow reactor. Sulfur poisoning and thermal aging are unavoidable factors contributing to diesel LNT deactivation. The results show that sensitivity to sulfur poisoning varies with the catalyst formulations, and in some formulations the sulfur poisoning appears reversible. However, the thermal deactivation is permanent regardless of its cause, i.e., LNT de-sulfation (deSOx) or diesel particular filter (DPF) regeneration.

An analytical model was developed to simulate both sulfur adsorption and desorption characteristics based on the laboratory determined parameters. Diesel Lean NOx Trap (LNT) was tested under laboratory conditions to examine desulfation (deSOx) characteristics. Effects of different Lean/Rich (L/R) cycling of Air-Fuel ratio during the deSOx mode were investigated. The gradient of adsorbed sulfur along the axial direction of the sample LNT was also examined. The gradient of sulfur deposit, together with different L/R cycling combinations for the deSOx mode was critical to develop the efficient sulfur removal strategies. The model considered energy and mass balances during sulfur adsorption and desorption modes to predict the catalyst temperature and the amount of sulfur adsorbed and removed. HC and CO oxidation reactions as well as the oxygen storage were considered to estimate heat generated by the exothermic reactions.