Among the various high strength steels available today, boron steels are finding increasing applications in bumper beams and other crash resistant structures, primarily for their high strength. However, to overcome the forming difficulty at room temperature and to achieve the microstructural changes needed for high strength, manufacturing of boron steel parts is done under hot forming conditions. In this study, the effect of three principal bumper design parameters, namely depth, thickness and corner radius on the formability of a hat section bumper beam was considered. Using a forming simulation program, 27 different combinations of these three design parameters were examined for forming limits, failure types and failure locations. The bumper beams were also examined for energy absorption in pendulum impact tests. Recommendations are made for the design of boron steel bumper beams based on both impact energy absorption and formability.

This paper describes an experimental work on the bending springback of aluminum alloy 5754. Experiments were performed using a 90° V-shaped matching die-punch combination, with and without clamping. Clamping was used to create tension during bending. The experimental parameters taken into account are the die radius, sheet clamping torque, sheet thickness and the level of cold work in the sheet.

This paper will present the results of 3-D finite element analyses of single lap adhesive joints between magnesium and three other automotive materials, namely steel, aluminum and SRIM composites. The modulus of magnesium is lower than that of either steel or aluminum, but is higher than that of SRIM. Thus, this study aims at determining the effect of the difference in substrate modulus on the deformation, stress and strain distributions and maximum stresses in adhesive joints of magnesium with the other three materials. In addition, the effect of adhesive modulus is also explored.

This paper presents a comparison of aqueous corrosion rates in 5% NaCl solution for eight experimental creep-resistant magnesium alloys considered for automotive powertrain applications, as well as three reference alloys (pure magnesium, AM50B and AZ91D). The corrosion rates were measured using the techniques of titration, weight loss, hydrogen evolution, and DC polarization. The corrosion rates measured by these techniques are compared with each other as well as with those obtained with salt-spray testing using ASTM B117. The advantages and disadvantages of the various corrosion measurement techniques are discussed.

This study utilized Rutherford Backscattering Spectroscopy (RBS) and Auger Electron Spectroscopy (AES) to determine the thickness and composition of corrosion films formed on magnesium alloys exposed to experimental engine coolants intended for use with creep-resistant magnesium alloy engine blocks. Knowledge on the nature of the film formed may produce a better understanding of corrosion inhibition and protection requirements for these materials. This paper will first briefly review the RBS and AES techniques as applied to the characterization of surface films on metals. It will then present results from experiments conducted with pure magnesium and two different magnesium alloys in two engine coolants.

This paper presents cost-benefit analysis of glass and carbon fiber reinforced thermoplastic matrix composites for structural automotive applications based on press forming operation. Press forming is very similar to stamping operation for steel. The structural automotive applications involve beam type components. The part selected for a case study analysis is a crossbeam support for instrument panels.

In frontal collision of vehicles, the front bumper system is the first structural member that receives the energy of collision. In low speed impacts, the bumper beam and the crush cans that support the bumper beam are designed to protect the engine and the radiator from being damaged, while at high speed impacts, they are required to transfer the energy of impact as uniformly as possible to the front rails that contributes to the occupant protection. The bumper beam material today is mostly steels and aluminum alloys, but carbon fiber composites have the potential to reduce the bumper weight significantly. In this study, crash performance of bumper beams made of a boron steel, aluminum alloy 5182 and a carbon fiber composite with steel crush cans is examined for their maximum deflection, load transfer to crush cans, total energy absorption and failure modes using finite element analysis.

This paper describes the results of dynamic denting experiments conducted on AA5754 and AA6061 alloys. Dynamic denting tests were performed using a drop weight impact machine. The drop height was varied from 38 mm to 914 mm to generate impact velocities ranging from 53.4 m/min to 254 m/min. The dent depth created at different drop heights was related to the input impact energy and peak load observed in the tests. The effects of sheet thickness and yield strength were explored.

Self-piercing riveting is a relatively new process for joining sheet metals in automotive applications. Its importance is growing in the automotive industry because of its advantages over spot welding aluminum alloys. One of these advantages is the higher fatigue strength, which is useful in designing body structures. This paper presents experimental data on the effects of several process variables, such as rivet diameter, rivet length, rivet hardness, sheet thickness and die shape, on the static and fatigue properties of self-piercing riveted joints in aluminum alloy 5754. Statistical analysis has been performed to examine the relative importance of these variables on the static and fatigue performance of the joints.

This study reports the performance of three different automotive magnesium substrate materials (AM60B diecastings, AZ31-H24 sheet, and AM30 extrusions), each bonded to a common aluminum reference material with two different toughened adhesives. The magnesium substrates were pretreated with six different commercial pretreatments both with and without a final fused-powder polymeric topcoat. These samples were then evaluated by comparing initial lap-shear strength to the lap-shear strength after cyclic-corrosion testing. Additionally, use of a scribe through the polymer primer permitted assessment of: 1) distance of corrosion undercutting from the scribe (filiform), and 2) percent corrosion over the area of the coupon. The results showed that the performance of each magnesium pretreatment varied on cast AM60B, sheet AZ31-H24, and extruded AM30 substrates.

This study considers the thermal stresses in single lap adhesive joints between magnesium and steel. The source of thermal stresses is the large difference in the coefficients of thermal expansion of magnesium and steel. Two different temperature differentials from the ambient conditions (23°C) were considered, namely -30°C and +50°C. Thermal stresses were determined using finite element analysis. In addition to Mg-steel substrate combination, Mg-Mg and steel-steel combinations were also studied. Combined effect of temperature variation and applied load was also explored. It was observed that temperature increase or decrease can cause significant thermal stresses in the adhesive layer and thermal stress distribution in the adhesive layer depends on the substrate combination and the applied load.

The effects of lubricant on lap shear strength of Spot Friction Welded (SFW) joints made of 6111-T4 alloys were studied. Taguchi L8 design of experiment methodology was used to determine the lubricant effects. The results showed that the lap shear strength increased by 9.9% when the lubricant was present at the top surface compared to that of the baseline (no lubricant) whereas the lap shear strength reduced by 10.2% and 10.9% when the lubricant was present in the middle and at the bottom surfaces compared to that of the baseline (no lubricant), respectively. The microstructure analysis showed a zigzag interface at the joint between the upper and the lower sheet metal for the baseline specimen, the specimens with the lubricant at the top and at the bottom. However, a straight line interface is exhibited at the joint between the upper and the lower sheet for the specimen with the lubricant in the middle. The weld nugget sizes of the lap shear tested specimens were measured.

This paper presents the results of fatigue tests conducted on tailor-welded aluminum blanks consisting of 1.66 mm thick and 1.06 mm thick AA 5754-O sheets. The method of joining the sheets was friction-stir welding. The primary purpose of this study was to determine the effect of tensile pre-strains on the fatigue performance of the welded joint. The welded specimens as well as unwelded 1.06-mm thick specimens were subjected to tensile pre-strains of 60 and 80% of their respective uniform strains before the fatigue tests. Fatigue S-N data of all these specimens were compared with similar data for unstrained specimens. Microscopic examinations were conducted to understand the failure modes.

Spot friction welding shows advantages over resistance spot welding for joining light alloys for automotive applications. In this research, fatigue behaviors of spot friction welded joints in lap shear specimens of AM-60 magnesium alloy and AA 5754 aluminum alloy were investigated. Static and fatigue tests were conducted with Mg-Mg, Al-Al and Al-Mg specimens. Fatigue S-N curves were obtained for all these specimens using load-controlled fatigue tests. Finite element analysis was conducted to investigate the stress distribution and the location of maximum stresses in spot friction welded joints in Mg-Mg specimens.

Owing to their weight saving potential and improved flexural stiffness, metal-polymer-metal sandwich laminates are finding increasing applications in recent years. Increased use of such laminates for automotive body panels and structures requires not only a better understanding of their mechanical behavior, but also their formability characteristics. This study focuses on the formability of a metal–polymer-metal sandwich laminate that consists of AA5182 aluminum alloy as the outer skin layers and polypropylene (PP) as the inner core. The forming limit curves of Al/PP/Al sandwich laminates are determined using finite element simulations of Nakazima test specimens. The numerical model is validated by comparing the simulated results with published experimental results. Strain paths for different specimen widths are recorded.

An experimental study was conducted to investigate the potential of spot joining aluminum with nylon using frictional heat. The process utilizes the heat generated by friction between a rotating tool surface and the aluminum sheet surface to melt nylon locally in the joining area and create a mechanical interlock between the aluminum and nylon sheets. Lap shear joint specimens were prepared using this process to investigate the effect of several parameters such as tool geometry, tool RPM, tool hold time, tool plunge depth and tool feed rate. Tensile tests were conducted to evaluate the joint strength and to investigate the failure mechanisms of the joint. Furthermore, the effects of cleaning the aluminum surface and baking of the nylon on the joint strength were also studied in this paper. Finally, friction heat generated joints were compared with adhesively bonded joints between aluminum and nylon.

A ductile failure criterion (DFC), which defines the stretching failure at localized necking (LN) and treats the critical damage as a function of strain path and initial sheet thickness, was proposed in a previous study. In this study, the DFC is revisited to extend the model to the low stress triaxiality domain and demonstrates on modeling forming limit curve (FLC) of TRIP 690. Then, the model is used to predict stretching failure in a finite element method (FEM) simulation on a TRIP 690 steel rectangular cup draw process at room temperature. Comparison shows that the results from this criterion match quite well with experimental observations.

Based on findings from micromechanical studies, a Ductile Failure Criterion (DFC) was proposed. The proposed DFC treats localized necking as failure and critical damage as a function of strain path and initial sheet thickness. Under linear strain path assumption, a method to predict Forming Limit Curve (FLC) is derived from this DFC. With the help of predetermined effect functions, the method only needs a calibration at uniaxial tension. The approach was validated by predicting FLCs for sixteen different aluminum and steel sheet metal materials. Comparison shows that the prediction matches quite well with experimental observations in most cases.

Sandwich panels with high modulus/high strength skin material and low density/low modulus core material have higher stiffness-to-weight ratio than monolithic panels. In this paper, sandwich panels with corrugated core are explored as a lightweighting concept for improved stiffness. The skin and the core materials are a high strength steel, aluminum alloy or carbon fiber-epoxy composite. The core has a triangular corrugation, a trapezoidal corrugation and a rectangular corrugation. The stiffness of the sandwich panels is analytically determined and compared with monolithic panels of equal mass. It is shown that the stiffness of the sandwich panels is 5 to 7 times higher than that of the monolithic panels.

Spot friction welding is considered a cost-effective method for joining lightweight automotive alloys, such as magnesium and aluminum alloys. An experimental study was conducted to investigate the strength of spot friction welded joints of magnesium to magnesium, aluminum to aluminum, magnesium to aluminum and aluminum to magnesium. The joint structures and failure modes were also studied.