To reduce heat transfer between hot gas and cavity wall, thin Zirconia (ZrO2) layer (0.5mm) on the cavity surface of a forged steel piston was firstly formed by thermal spray coating aiming higher surface temperature swing precisely synchronized with flame temperature near the wall resulting in the reduction of temperature difference. However, no apparent difference in the heat loss was analyzed. To find out the reason why the heat loss was not so improved, direct observation of flame impingement to the cavity wall was carried out with the top view visualization technique, for which one of the exhaust valves was modified to a sapphire window. Local flame behavior very close to the wall was compared by macrophotography. Numerical analysis by utilizing a three-dimensional simulation was also carried out to investigate the effect of several parameters on the heat transfer coefficient.

This study investigates simultaneous improvement in thermal efficiency and cooling loss in the wider operating condition. To suppress the heat flux of the piston, the piston top and cavity were treated with thin thermal spraying of stainless steel. Thermal diffusivity of stainless steel (X5CrNiMo17-12-2, SUS316) is very low in comparison with the forged steel piston raw material (34CrMoS4, SCM435) to sustain local surface temperature at where spray flame directly interfered. In addition, its surface roughness was very fine finished aiming to reduce the convective heat transfer. The experimental results with the stainless-steel coated piston by utilizing a single cylinder engine showed the significant improvement in both cooling loss and thermal efficiency even in higher load operating conditions with compression ratio of 23.5:1.