Corrosive wear of non-ferrous engine components by lubricants is a concern of all major heavy duty diesel engine manufacturers since warranty on key engine components has been extended to 500,000 miles. Several commercial lubricants have been linked to premature cam and rod bearing failures induced by corrosion in certain fleets. Although the overall failure rate is low, specific fleets have experienced significantly higher failure rates due to the lubricants used. These failures usually occur at high mileages but less than 500,000 miles. This kind of slow corrosion easily escapes detection of engine tests contained in current oil specifications, and it represents a serious issue in long term warranty cost to diesel engine manufacturers. A comprehensive fleet database has been established to identify the most corrosive lubricants. These lubricants have served as reference oils to develop a corrosion bench test.

Sulfur poisoning from engine fuel and lube is one of the most recognizable degradation mechanisms of a NOx adsorber catalyst system for diesel emission reduction. Even with the availability of 15 ppm sulfur diesel fuel, NOx adsorber will be deactivated without an effective sulfur management. Two general pathways are currently being explored for sulfur management: (1) the use of a disposable SOx trap that can be replaced or rejuvenated offline periodically, and (2) the use of diesel fuel injection in the exhaust and high temperature de-sulfation approach to remove the sulfur poisons to recover the NOx trapping efficiency. The major concern of the de-sulfation process is the many prolonged high temperature rich cycles that catalyst will encounter during its useful life. It is shown that NOx adsorber catalyst suffers some loss of its trapping capacity upon high temperature lean-rich exposure.