This specification covers an aluminum alloy in the form of bars and rods 0.500 inch (12.7 mm) to 8.000 inches (203.2 mm) in nominal diameter or least difference between parallel sides and up to 50 square inches (322.6 square centimeters) in cross-sectional area (see 8.7).
This specification covers an aluminum-lithium alloy in the form of extruded profiles with a maximum cross-sectional area of 19 in2 (123 cm2) and a maximum circle size of 11 inches (279 mm) from 0.040 to 0.499 inch (1.00 to 12.50 mm) in thickness (see 8.7).
This specification covers pure gold in the form of wire 0.005 to 0.040 inch (0.012 to 1.000 mm) inclusive, in nominal diameter, and ribbon 0.002 to 0.051 inch (0.05 to 1.28 mm) inclusive, in nominal thickness (see 8.5).
This specification covers an aluminum alloy in the form of extruded bars, rods, and profiles (shapes) with a maximum cross-sectional area of 25 in2 (161 cm2), a maximum circle size of 12 inches (305 mm) and a nominal thickness up to 3.250 inch (82.54 mm), inclusive.
This specification covers an aluminum alloy in the form of rolled or forged rings up to 8 inches (203 mm), inclusive, in nominal thickness at the time of heat treatment, and having an OD to wall thickness ratio of 10 or greater (see 8.6).
This specification covers an aluminum alloy in the form of extruded bars, rods, and profiles (shapes) from 0.375 to 1.300 inches (9.53 to 33.02 mm) in diameter or thickness, produced with cross sectional area of 22.5 in2 (145 cm2) maximum, and a circumscribing circle diameter (circle size) of 17.4 inches (44.2 cm) maximum. See 8.3 for definition of circumscribing circle size.
1.1 Form This specification covers an aluminum alloy procured in the form of sheet 0.078 to 0.197 inch (2.00 to 5.00 mm), inclusive, in nominal thickness, Alclad on both sides (see 8.5). 1.2 Application These products have been used typically for formed structural parts requiring good formability in T4 temper and ability to develop improved resistance to fatigue crack growth and high toughness with moderate strength when aged to T62 temper, but usage is not limited to such applications.