Effects of Processing Time on Strengths and Failure Modes of Dissimilar 5754/7075 and 7075/5754 Spot Friction Welds in Lap-Shear Specimens 2008-01-1138

In this investigation, dissimilar 5754/7075 and 7075/5754 spot friction welds were first made under different processing conditions. The spot friction welds in lap-shear specimens were tested under quasi-static loading conditions. The optimal processing times to maximize the failure loads of the 5754/7075 and 7075/5754 welds under lap-shear loading conditions are identified. The maximum failure load of the 7075/5754 welds is about 40% larger than that of the 5754/7075 welds. Optical micrographs of both types of spot friction welds made at different processing times before and after failure are examined. The micrographs show different weld geometries and different failure modes of spot friction welds made at different processing times. The failure modes of the 5754/7075 and 7075/5754 spot friction welds appear to be quite complex and strongly depend on the geometry and the strength of the interfacial surface between the two deformed sheet materials.