Search Results

Model low temperature NOx adsorbers (LTNA) consisting of Pd on a ceria/zirconia washcoat on monoliths were evaluated for low temperature NOx storage under lean conditions to assess their potential for adsorbing the cold-start NOx emissions on a diesel engine during the period before the urea/SCR system becomes operational. A reactor-based transient test was performed with and without C2H4, CO/H2, and H2O to assess the effects of these species on the NOx storage performance. In the absence of C2H4 or CO/H2, H2O severely suppressed the NOx storage of these model LTNAs at temperatures below 100°C, presumably by blocking the storage sites. When C2H4 was included in the feedgas, H2O still suppressed the NOx storage below 100°C. However, the C2H4 significantly increased the NOx storage efficiency above 100°C, attributable to the formation of alkyl nitrites or alkyl nitrates on the catalyst.

In anticipation that future gasoline engines will have improved fuel efficiency and therefore lower exhaust temperatures during low load operation, a project was initiated in 2014 to develop three-way catalysts (TWC) with improved activity at lower temperatures while maintaining the durability of current TWCs. This project is a collaboration between Ford Motor Company, Oak Ridge National Laboratory, and the University of Michigan and is funded by the U.S. Department of Energy. The ultimate goal is to show progress towards the USDRIVE goal of 90% conversion of hydrocarbons (HC), carbon monoxide (CO), and nitrogen oxides (NOx) at 150°C after high mileage aging. A reactor was set up at Ford to follow the catalyst testing protocols established by the USDRIVE ACEC tech team for evaluating catalysts for stoichiometric gasoline direct-injection (S-GDI) engines; this protocol specifies a stoichiometric blend of CO/H2, NO, C3H6, C2H4, C3H8, O2, H2O, and CO2 for the evaluations.

Selective catalytic reduction (SCR) is a viable option for control of oxides of nitrogen (NOx) from diesel engines. Currently, copper zeolite (Cu-zeolite) SCR catalysts are favored for configurations where the exhaust gas temperature is below 450°C for the majority of operating conditions, while iron zeolite (Fe-zeolite) SCR catalysts are preferred where NOx conversion is needed at temperatures above 450°C. The selection of Cu-zeolite or Fe-zeolite SCR catalysts is based on the different performance characteristics of these two catalyst types. Cu-zeolite catalysts are generally known for having efficient NOx reduction at low temperatures with little or no NO2, and they tend to selectively oxidize ammonia (NH3) to N2 at temperatures above 400°C, leading to poor NOx conversion at elevated temperatures.

Selective Catalytic Reduction of NOx is a promising technology to enable diesel engines to meet certification under Tier 2 Bin 5 emissions requirements. SCR catalysts for vehicle use are typically zeolitic materials known to store both hydrocarbons and ammonia. Ammonia storage on the zeolite has a beneficial effect on NOx conversion; hydrocarbons however, compete with ammonia for storage sites and may also block access to the interior of the zeolites where the bulk of the catalytic processes take place. This paper presents the results of laboratory studies utilizing surrogate hydrocarbon species to simulate engine-out exhaust over catalysts formulated to operate in both low (≈175-500°C) and high temperature (≈250-600°C) regimes. The effects of hydrocarbon exposure of these individual species on the SCR reaction are examined and observations are made as to necessary conditions for the recovery of SCR activity.

Selective catalytic reduction (SCR) is a technology capable of meeting Tier 2 Bin 5 emissions levels of oxides of nitrogen (NOX) for diesel engines. Base metal zeolite catalysts show the best combination of thermal durability and NOX conversion activity. It is shown in this work that some base metal zeolite catalysts can store high levels of hydrocarbons (HCs). Also, base metal zeolite catalysts can catalyze oxidation of HCs under certain conditions. Oxidation of stored hydrocarbons can lead to permanent catalyst deactivation due to the exotherm generated in the SCR catalyst (over-temperature condition leading to SCR catalyst damage). This paper discusses a laboratory bench test to characterize hydrocarbon storage and burn-off characteristics of several SCR catalyst formulations, as well as engine dynamometer tests showing hydrocarbon storage and exotherm generation.