Search Results

A bench engine test for evaluating the fuel efficiency of automotive crankcase oils using modern engines was developed. The fuel consumption was primarily proportional to the viscosity of the oils down to 5 mm2/s at operating temperatures, indicating that the use of low-viscosity oil was effective in improving fuel efficiency. This may be because the oil film would be formed easily, since sliding parts, such as valve train systems, in modern engines are finely finished. Organo molybdenum dithiocarbamates were effective in improving fuel efficiency at high temperature. A 2.7% improvement in fuel efficiency relative to conventional SAE 10W-30 oils was achieved by the combination of low-viscosity SAE 5W-20 oils and organo molybdenum dithiocarbamates under constant operating conditions with engine speed 1,500 rpm and torque 37.2 N•m.

It is widely known that pellet-typed catalysts are deactivated by phosphorus (ZnDTP) that comes from engine oils. In this paper, the poisoning of monolithic three-way catalysts and oxygen sensors by engine oils is studied. First, catalysts and oxygen sensors were poisoned on the engine bench by test oils in which the quantity of phosphorus and ash was varied. Next, performance of the catalysts and sensors alone was examined and the vehicle exhaust emission at FTP mode was measured on a chassis dynamometer. The results indicate that phosphorus in engine oils poisons the monolithic catalyst and the oxygen sensor resulting in deterioration of the vehicle NOx exhaust emission. However, Ca sulfonate and Mg sulfonate detergents act by restraining phosphorus poisoning of the catalyst and the oxygen sensor. Through analysis of the catalyst and sensor surfaces, it is concluded that phosphorus poisons the catalyst and sensor forming a dense coating.

The influence of engine oil viscosity on the wear of piston rings and cam faces has been investigated by fired engine tests using a radioisotope (RI) tracer technique. High-temperature and high-shear-rate (HTHS; 150°C, 1O6 s-1) viscosities of the experimental oils prepared are 2.2, 2.4, 2.6 and 3.1 mPa•s. At an oil temperature of 90°C the wear of piston rings and cam faces did not increase, even if the HTHS viscosity was lowered down to 2.2 mPa•s. However, both piston rings and cam faces exhibited an increase in wear below 2.4 mPa•s at 130°C. It was also recognized that valve train wear did not significantly increase with reducing viscosity in the motored engine tests at a temperature of 50°C. From these test results, it was suggested that the oil with the HTHS viscosity of 2.6 mPa•s sufficiently demonstrates the antiwear performance equivalent to that with around 3.0 mPa•s for application to piston rings and cam faces.

The effect of phosphorus concentration in gasoline engine oils on the valve train wear was experimentally investigated by using the JASO M328-91 3A valve train wear (3A-VTW) test method. The phosphorus concentration is determined proportionally to the amount of zinc dithiophosphate (ZDDP), which is formulated as both antiwear agent and antioxidant. Lower concentrations of ZDDP generally bring about larger wear in the valve train. However, it was found from the experiments that valve train wear remained low despite a decrease of phosphorus concentration when secondary ZDDPs with short alkyl chain together with appropriate ashless dispersants were selected. Since adsorptivity of secondary ZDDPs with short alkyl chain lengths onto rubbing metal surfaces is higher than that of primary types, the secondary types give excellent antiwear characteristics.