This specification covers a precipitation hardenable, corrosion- and heat-resistant nickel alloy in the form of seamless tubing 0.125 inch (3.18 mm) and over in nominal OD and 0.015 inch (0.38 mm) and over in nominal wall thickness.
This document covers the recommended practice for determining the acceptability of the dendrite arm spacing (DAS) of D357-T6 aluminum alloy castings required to have tensile strength not lower than 50 ksi (345 MPa).
This document defines a recommended practice for addressing metal additive manufacturing (AM) machine requalification for all fusion-based metal AM machines. In general, this applies to powder bed fusion (PBF) and wire- or powder-fed directed energy deposition (DED) technologies. Plasma, electron beam, or lasers are applicable energy source(s).
This document covers all metal, self-locking wrenching nuts, plate nuts, shank nuts, and gang channel nuts made from a corrosion and heat resistant steel of the type identified under the Unified Numbering System as UNS S66286 and of 160 ksi tensile strength at room temperature, with maximum test temperature of parts at 1200 °F.
This procurement specification covers aircraft quality self-locking nuts for wrenching (hex, spline) and anchor (plate, gang channel, shank) types of nuts made from a corrosion and heat-resistant nickel-base alloy of the type identified under the Unified Numbering System as UNS N07001. Tension height nuts having overall length of threaded portion not less than 1.2 times the nominal thread diameter have 1210 MPa minimum tensile strength at room temperature. Shear height nuts having shorter threaded portion have 1100 MPa minimum tensile strength at room temperature. Maximum test temperature of parts is 730 °C.
SAE J3108 RP provides fuel and hazard guidance for first and second responders of incidents associated with alternative fueled vehicles. The intent of this SAE J3108-1 RP is to remain with the limited number of seven intuitive and colored letters contained in each of the first two letter positions (72=49). However, the use of four letters plus nine digits (to not use either 0 or o) permits up to 1185921 unique identifiers (334) for future expansion. The RP is not intended to replace the standards for SAE J2990 format emergency response guide (ERG) created by automotive manufacturers for use at the scene of an emergency. Automotive OEMs are encouraged to reference this RP for industry design guidance when creating vehicle requirements and ERGs. This coding should be consistent with other vehicle badging with the goal of providing additional clarity.
This specification covers a magnesium alloy in the form of sheet and plate from 0.016 to 3.000 inches (0.41 to 76.20 mm), inclusive, in thickness (see 8.5).
This specification covers a magnesium alloy in the form of extruded bars, rods, wire, tubing, and profiles up to 40 square inches (258 cm2) in cross-sectional area (solids) and up to 8.5 inches (216 mm) OD by 1.188 inches (30.18 mm) wall thickness (tubing) (see 8.5).
This specification establishes the requirements for flake or granular cetyl alcohol, solvents for dissolving the cetyl alcohol, preparation and application requirements for use of cetyl alcohol as an installation lubricant on mechanical fasteners, such as pins, bolts, nuts, washers, threaded or nonthreaded fastening devices, and inspection criteria for coated parts.
This specification covers an aluminum alloy in the form of alclad sheet over 0.039 to 0.126 inches (0.99 to 3.20 mm), inclusive, in nominal thickness with a fine-grain core of ASTM No. 6 or finer (see 8.5).
This specification covers an aluminum alloy in the form of extruded rods, bars, and profiles (shapes) 0.040 to 1.500 inches (1.02 to 38.10 mm), inclusive, in thickness, and produced with maximum cross-sectional area of 23.25 square inches (15000 mm2) and a maximum circumscribing circle diameter (circle size) of 15.5 inches (394 mm) (see 2.4.1 and 8.6).
This specification covers an aluminum alloy in the form of sheet and plate 0.017 to 2.000 inches (0.43 to 50.80 mm), inclusive, in nominal thickness (see 8.6).