The influence of elevated temperature forming on local mechanical properties of AZ31B magnesium (Mg) sheet material was investigated. The Mg sheet was formed into a closure component with high temperature gas pressure at 485°C. Miniature tensile testing specimens were cut from selected areas of the component where different levels of thinning occurred. The specimens were strained in tension to fracture using a miniature tensile stage. The two-dimensional strain distribution in the necking region along with true stress-true strain curves were computed using a digital image correlation technique to assess the influence of the forming-induced thinning on tensile strength and percent elongation at fracture.

A methodology that enables two-dimensional strain field measurement in the vicinity of ductile rupture is described. Fully martensitic steel coupons were strained to fracture using a miniature tensile stage with custom data and image acquisition systems. Rupture initiated near the center of each coupon and progressed slowly toward the gage section edges. A state-of-the-art digital image correlation technique was used to compute the true strain field before rupture initiation and ahead of the resulting propagating macroscopic crack before final fracture occurred. True strains of the order of 95% were measured ahead of the crack at later stages of deformation.

Tensile measurements and fracture surface analysis of low carbon heat-treated boron steel are reported. Tensile coupons were quasi-statically deformed to fracture in a miniature tensile testing stage with custom data acquisition software. Strain contours were computed via a digital image correlation method that allowed placement of a digital strain gage in the necking region. True stress-true strain data corresponding to the standard tensile testing method are presented for comparison with previous measurements. Fracture surfaces were examined using scanning electron microscopy and the deformation mechanisms were identified.