Search Results

Diesel engine operation under high load conditions (>45 hp/cyl) may result in piston “debond” in which the Ni-resist ring carrier separates from the aluminum piston matrix leading to destruction of the piston. Historically, engine loads have increased to achieve higher power densities which together with more stringent emissions requirements have resulted in greatly increased stress levels in the piston. The higher stresses have resulted in debond failure. The design of the ring carrier will affect debond failure. Deformation of the ring carrier will initiate debond at the back of the insert at the junction with the piston matrix. The ring carrier cross-section must be made robust enough through proper design to achieve expected reliability. Another factor influencing ring carrier retention is the quality of the AlFin bond layer. Casting defects which arise from the AlFin bonding process, degrade the strength of the joint leading to failure.

High Velocity Oxygen Fuel sprayed face coatings have shown great promise for piston rings used for High Power Density Diesel Engines. Various coatings have been tested on both wear test rigs and in engines. A highly dense HVOF cermet coating was developed with reasonable crack resistance during service. The HVOF coated piston rings wore three to six times lower than chrome plating. Cylinder liner (counter face) wear was found to be one to three times higher than chrome. However, engine oil consumption and blow by were within normal values. The HVOF coating is considered to be an excellent replacement for chrome plating. The coating process is more environmentally friendly than the chrome plating process. Also, the coating has potentially lower or equivalent production cost when compared to chrome.

A laboratory method has been developed to rank the scuff resistance of piston ring coatings. This method employs a standard wear test apparatus with a specially designed sample holder. Scuff resistance of electrolytic chrome, thermal spray and physical vapor deposition (PVD) face coatings have been examined. Based on this method, examined PVD coatings produced the highest scuff resistance of all the tested face coatings.

The ability of a piston oil ring to conform to liner distortions during engine operation is directly related to its radial stiffness. The ability to conform is also very important for controlling lubricant oil consumption and emissions. This paper describes the procedure utilized to investigate the technical feasibility of using flexible high performance engineering plastics to replace metal as base material for oil rings. Bench tests and engines were used to select and evaluate different types of plastics for wear resistance and structural integrity. Engine test results indicated no structural failures but wear levels were found to be unacceptably high for use in durable heavy duty diesel engines.

Diesel engine builders are faced with a new challenge to lower the weight of engines to increase payload while meeting rigorous durability goals for the engine. Cooling system parts represent a family of components which may be converted to lightweight metallic alloys for significant weight savings. To utilize lightweight alloys, cooling system parts must be engineered to maintain the same durability as the cast iron components they replace. For a modern high speed diesel, the Bl0 design life may be upwards of 1,280,000 kilometers which is a very aggressive target for a new component design. A test program was planned to guide design and development of aluminum (Al) cooling system parts for a new engine. The part must exhibit no corrosion after long duration operating with acceptable coolant. This program included three major phases consisting of bench scale corrosion tests for alloy selection, component rig tests for design verification and engine testing for system reliability.

A high horsepower, low heat rejection diesel engine is being developed to meet future Army heavy combat vehicle requirements. This engine features high power output in a compact design that is oil-cooled allowing for a significant reduction in radiator size. This design requires a lubricant which can survive a sump temperature of 160°C, for 300 hours with transient sump temperature surges to over 177°C. A comprehensive high temperature lubricant development program has been initiated to address the need for this new design. A modified Cummins 10 liter diesel engine was used to simulate the operating condition of this low heat rejection engine. The premium commercial lubricant that was tested survived only 58 hours before completely losing oxidative stability. Several of the experimental lubricants completed the 200-hour peak torque endurance test.

This work evaluates the thermal and structural integrity of a heavy duty diesel piston using finite element analysis. The effects of aluminum, ductile iron, and superalloy piston materials; air gaps; and plasma-sprayed zirconia coating on piston temperature and stress, as well as on heat flux through the piston, are assessed. The coating lowered the heat flux through the piston 56 percent and caused other changes in the piston to have an insignificant effect on the heat flux. The air gaps had the least effect on heat flux with substantially lower safety margins than pistons without air gaps.

The ongoing need for improved fuel economy, longer engine life, lower emissions, and in some cases, increased power output makes lower charge air temperatures more desirable. In 1983, Cummins introduced the new BCIV engine at 400 H.P. (298 KW) with “Optimized Aftercooling”, and is now introducing this concept to its remaining 10 and 14 Litre premium diesel engines. This Tuned Low Flow Cooling design provides many advantages when compared to the other alternatives studied, which included air-to-air and systems incorporating two radiators. The selection process considered performance, durability, fuel economy, emissions, noise, investment, and total vehicle installed cost. Computer simulations and vehicle tests were used to determine performance for each charge air cooling alternative. The simulations were used to guide prototype development and the selection of production hardware.

Laboratory tests have shown that 40% glass-reinforced PPS is suitable for automotive underhood use where it comes into contact with used engine oil, gasoline/alcohol, gasoline/MTBE, water, water/ethylene glycol, hydraulic fluid, and transmission fluid at elevated temperatures. On exposure to water or water/ethylene glycol at 248° F (120° C) and 257°F (125°C), respectively, there is a sharp decline in mechanical strength in the first few weeks with little change thereafter. The residual strength of the 40% glass-reinforced PPS is comparable to, or better than other materials, such as phenolics, which have proved satisfactory in such usage. These results have been translated to successful applications in heavy duty diesel engines. Piston cooling nozzles and water pump impellers made of 40% glass-reinforced PPS have undergone successful engine component evaluations.