The performance characteristics of a commercial lean-NOX trap catalyst were evaluated between 200 and 500°C, using H2, CO, and a mixture of both H2 and CO as reductants before and after different high-temperature aging steps, from 600 to 750°C. Tests included NOX reduction efficiency during cycling, NOX storage capacity (NSC), oxygen storage capacity (OSC), and water-gas-shift (WGS) and NO oxidation reaction extents. The WGS reaction extent at 200 and 300°C was negatively affected by thermal degradation, but at 400 and 500°C no significant change was observed. Changes in the extent of NO oxidation did not show a consistent trend as a function of thermal degradation. The total NSC was tested at 200, 350 and 500°C. Little change was observed at 500°C with thermal degradation but a steady decrease was observed at 350°C as the thermal degradation temperature was increased.

Advanced flow-reactor capabilities created at Cummins were applied to the study of the diesel particulate matter (soot) oxidation process. This approach complemented the on-engine studies with a number of important features, including accurate control of gas composition and soot layer temperature. Using the developed methodology for quantitative soot oxidation studies in a broad range of temperatures (200-700°C), an initial set of experiments was performed to compare the behavior of the real and model soot samples under the identical conditions (10%vol. of O2, 0-15%vol. of H2O). It was found that presence of H2O vapor synergistically enhances the rate of oxidation by O2 of the diesel soot sample. However, the behavior of the model soot sample (carbon black) was virtually not affected by H2O. Kinetic analysis of the obtained results revealed an unusual type of behavior, with the activation energy of soot oxidation increasing in the course of the experiment.