Failure mode and fatigue behavior of dissimilar laser welds in lap-shear specimens of aluminum and copper sheets are investigated. Quasi-static tests and fatigue tests of laser-welded lap-shear specimens under different load ranges with the load ratio of 0.1 were conducted. Optical micrographs of the welds after the tests were examined to understand the failure modes of the specimens. For the specimens tested under quasi-static loading conditions, the micrograph indicates that the specimen failed through the fusion zone of the aluminum sheet. For the specimens tested under cyclic loading conditions, two types of failure modes were observed under different load ranges. One failure mode has a kinked crack initiating from the interfacial surface between the aluminum and copper sheets and growing into the aluminum fusion zone at an angle close to 90°.

Failure mode of laser welds in lap-shear specimens of high strength low alloy (HSLA) steel is investigated in this paper. The experimental results from quasi-static tests show that the laser welds failed in a ductile necking/shear failure mode near the heat affected zone. In order to understand the failure mode of these welds, a finite element analysis under plane strain conditions was conducted to identify the effects of the different plastic behaviors of the base metal, heat affected zone, and weld metal on the ductile failure. The results of the finite element analysis show that the higher effective stress-plastic strain curves of the weld metal and the heat affected zone results in the necking/shear failure mode. The deformed shape of the finite element model near the weld matches well with that of a failed weld.