Fatigue behavior of laser welds in lap-shear specimens of high strength low alloy (HSLA) steels is investigated based on a fatigue crack growth model. Fatigue experiments of laser welded lap-shear specimens were conducted. Analytical global stress intensity factor solutions are developed and compared with finite element computational results. A fatigue crack growth model based on the analytical local stress intensity factor solutions of kinked cracks and the Paris law for crack growth is then adopted to estimate the fatigue lives of the laser welds under cyclic loading conditions. The estimated fatigue lives are compared with the experimental results. The results indicate that the fatigue life predictions based on the fatigue crack growth model are slightly longer than the experimental results.

Microstructures and failure mechanisms of spot friction welds (SFW) in aluminum 5754 lap-shear specimens were investigated. In order to study the effect of tool geometry on the joint strength of spot friction welds, a concave tool and a flat tool were used. In order to understand the effect of tool penetration depth on the joint strength, spot friction welds were prepared with two different penetration depths for each tool. The results indicated that the concave tool produced slightly higher joint strength than the flat tool. The joint strength did not change for the two depths for the flat tool whereas the joint strength slightly increases as the penetration depth increases for the concave tool. The experimental results show that the failure mechanism is necking and shearing for the spot friction welds made by both tools. The failure was initiated and fractured through the upper sheet under the shoulder indentation near the crack tip.