Search Results

In automotive body manufacturing the dies for blanking/trimming/piercing are under most severe loading condition involving high contact stress at high impact loading and large number of cycles. With continuous increase in sheet metal strength, the trim die service life becomes a great concern for industries. In this study, competing trim die manufacturing routes were compared, including die raw materials produced by hot-working (wrought) vs. casting, edge-welding (as repaired condition) vs. bulk base metals (representing new tools), and the heat treatment method by induction hardening vs. furnace through-heating. CaldieTM, a Uddeholm trademarked grade was used as trim die material. The mechanical tests are performed using a WSU developed trimming simulator, with fatigue loading applied at cubic die specimen’s cutting edges through a tungsten carbide rod to accelerate the trim edge damage. The tests are periodically interrupted at specified cycles for measurement of die edge damage.

During the extensive testing under NATO and Commercial Standards, crack is observed in camshaft housing to initiate from the eccentric shaft bore and go toward the hold down bolt hole. Hence lab test proposal is originated to induce similar failure in a controlled method and then to compare new design alternatives. CAE analysis follows the same set up as the lab test to duplicate failure mode in stress analysis and fatigue analysis with duty cycle loads, and then figures out two strategies on how to improve the design, including geometry change and material change. In geometry wise, four new design iterations are evaluated for comparison. In material wise, one new material for camshaft housing and five manufacturing effect parameters for pin and rocker arm are compared, including ground, machined, machined and decarburization, casting, as well as casting and nitride. With those comparisons, all manufacturing parameters are compared based on effectiveness to affect the fatigue life.

Additive manufacturing (AM) of metals is finding numerous applications in automotive industry. In 21st century, aluminum is second to steel in automotive sector, because of its high strength to weight ratio. Hence developing AM for aluminum alloys become necessary to make sure industry gains maximum benefit from AM. This study specifically deals with the manufacturing of Al 7050 alloy, which is quite hardest alloy to manufacture using AM. The ultimate goal is to optimize the laser deposition parameters to deposit defect free Al 7050 alloy on rolled aluminum alloy substrate. Parameter optimization (laser power, powder flow rate, and scanning speed) gets difficult with the presence of various low melting and boiling point alloying elements such as Zn, Mg etc. Numerous other challenges faced while depositing Al 7050 alloy, are also briefly discussed in this article. Microstructural investigation using optical and scanning electron microscopy confirms greater than 99% component density.

Safety performance of an experimental windshield with a thin, chemically tempered inner pane is compared with the standard windshield and other experimental windshields. The chemically tempered windshield has a penetration velocity of 35 mph compared with 26 mph penetration velocity for the standard windshield and has lower peak head accelerations than other types used in the experiments. The windshield tested produces a bulge on impact, which decelerates the head over a long distance with low accelerations. The bulge or pocket is lined with particles that are less lacerative than the standard annealed glass.