A high output experimental single cylinder diesel engine that was fully coated and insulated with a ceramic slurry coated combustion chamber was tested at full load and full speed. The cylinder liner and cylinder head mere constructed of 410 Series stainless steel and the top half of the articulated piston and the cylinder head top deck plate were made of titanium. The cylinder liner, head plate and the piston crown were coated with ceramic slurry coating. An adiabaticity of 35 percent was predicted for the insulated engine. The top ring reversal area on the cylinder liner was oil cooled. In spite of the high boost pressure ratio of 4:1, the pressure charged air was not aftercooled. No deterioration in engine volumetric efficiency was noted. At full load (260 psi BMEP) and 2600 rpm, the coolant heat rejection rate of 12 btu/hp.min. was achieved. The original engine build had coolant heat rejection of 18.3 btu/hp-min and exhaust energy heat rejection of 42.3 btu/hp-min at full load.

High-pressure fuel injection combustion is being applied as an approach to increase the power density of diesel engines. The high-pressure injection enables higher air utilization and thus improved smoke free low air-fuel ratio combustion is obtained. It also greatly increases the injection rate and reduces combustion duration that permits timing retard for lower peak cylinder pressure and improved emissions without a loss in fuel consumption. Optimization of these injection parameters offers increased power density opportunities. The lower air-fuel ratio is also conducive to simpler air-handling and lower pressure ratio turbocharger requirements. This paper includes laboratory data demonstrating a 26 percent increase in power density by optimizing these parameters with injection pressures to 200 mPa.

Thin thermal barrier ceramic coatings were applied to a standard production direct injection diesel engine. The resultant fuel economy when compared to the standard metallic engine at full load and speed (2600) was 6% better and 3.5% better at 1600 RPM. Most coated diesel engines todate have not shown significant fuel economy one way or the other. Why are the results more positive in this particular case? The reasons were late injection timing, high injection pressure with high injection rates to provide superior heat release rates with resultant lower fuel consumption. The recent introduction of the high injection pressure fuel injection system makes it possible to have these desirable heat release rates at the premixed combustion period. Of course the same injection characteristics were applied to the standard and the thin thermal barrier coating case. The thin thermal barrier coated engine displayed superior heat release rate.