A unique opportunity arose to make a direct comparison of aluminum, sheet molding compound (SMC) and steel using a common hood design. In considering all possible material combinations of inner and outer panels, it was discovered that some of the combinations were incompatible due to material properties. Only the compatible material combinations were considered. Three different joining techniques - welding, bonding and bonded hem flanging - were evaluated. The cost, weight and structural performance of the chosen hood material combinations were established. Areas of further development were identified, including design optimization for specific material combinations.

A selection of commercially available chromium and chromium-free post phosphate rinses along with a deionized water rinse were evaluated over several zinc and zinc-alloy coated sheet steels. The test specimens were pretreated and electrocoated on-line in an automotive assembly plant. The effect of the rinse treatments on the cosmetic corrosion performance of the substrates, after 5 years of exposure in an outdoor scab corrosion test was determined. After this exposure none of the rinse treatments had performed better than deionized water rinse on zinc and zinc-iron coated sheet. The zinc-nickel coating showed improved scribe creepage when treated with the Cr+6/Cr+3 rinse. Data is provided comparing the concentration of the treatments used vs scribe creepage and chipping corrosion paint loss.

A comprehensive selection of automotive sheet steels were exposed in an outdoor scab corrosion test to provide a base-line of cosmetic corrosion performance. Eighteen different coated sheet steels along with CRS as a control were processed using two commercially available zinc phosphate chemistries. The phosphating was done using both immersion and spray phosphate processes in a laboratory and an automotive assembly plant. Scribe creepage results are reported for 5 years outdoor scab exposure. Comparisons of the scribe creepage behavior of CRS, zinc, and zinc alloy coatings and the effect of the phosphate treatment are provided. An estimate of 10 years field performance is made.

Fastener failure due to hydrogen embrittlement is of significant concern in the automotive industry. These types of failures occur unexpectedly. They may be very costly to the automotive company and fastener supplier, not only monetarily, but also in terms of customer satisfaction and safety. This paper is an overview of a program which one automotive company initiated to minimize hydrogen embrittlement in fasteners. The objectives of the program were two-fold. One was to obtain a better understanding of the hydrogen embrittlement phenomena as it relates to automotive fastener materials and processes. The second and most important objective, was to eliminate hydrogen embrittlement failures in vehicles. Early program efforts concentrated on a review of fastener applications and corrosion protection systems to optimize coated fasteners for hydrogen embrittlement resistance.