Search Results

Quasi-static tensile properties of TRIP590 steels from three different manufacturers were investigated using digital image correlation (DIC). The focus was on the post-uniform elongation behavior which can be very different for steels of the same grade owing to different manufacturing processes. Miniature tensile specimens, cut at 0°, 45°, and 90° relative to the rolling direction, were strained to failure in an instrumented tensile stage. True stress-true strain curves were computed from digital strain gages superimposed on digital images captured from one gage section surface during tensile deformation. Microstructural phases in undeformed and fracture specimens were identified with optical microscopy using the color tint etching process. Fracture surface analyses conducted with scanning electron microscopy and energy dispersive spectroscopy were used to investigate microvoids and inclusions in all materials.

Forming Limit Curves (FLCs) were developed for the 5083 aluminum alloy at conditions simulating high temperature processes such as superplastic and quick plastic forming. Sheet samples were formed at 450 °C and at a constant strain rate of 5x10-3 s-1, by free bulging into a set of elliptical die inserts with different aspect ratios. Friction-independent formability diagrams, which distinguish between the safe and unsafe deformation zones, were constructed. Although the formability diagrams were confined to the biaxial strain region (right side quadrant of an FLD), the elliptical die insert methodology provides formability maps under conditions where traditional mechanical stretching techniques are limited.

Accurate material property data in both the elastic and plastic ranges of deformation is essential for accurate material representation in finite element simulations of vehicle systems. Variation of post formed material properties across a part are often of interest in different types of analyses, such as metal forming or fatigue life, for example. Depending on a part's shape it is not always possible to cut standard size tensile test specimens from all areas of interest across the part. Smaller size specimens with curved or tapered gage section may have to be used to promote strain localization and fracture at or near the gage center. This paper presents comparison of quasi-static tensile properties determined using two specimen gage section geometries, straight and tapered. Specifically, the following questions are addressed. How do the engineering strains computed from two-dimensional strain fields obtained by DIC compare to strains measured during standard tensile tests?

Temperature effects on the deformation and fracture of a commercially produced transformation-induced plasticity (TRIP) steel subject to a two-step quenching and partitioning (Q&P) heat treatment are investigated. Strain field evolution at room temperature is quantified in this 980 MPa grade Q&P steel with a stereo digital image correlation (DIC) technique from quasi-static tensile tests of specimens with 0°, 45°, and 90° orientations. Baseline tensile properties along with the variation of the instantaneous hardening index with strain were computed. Variations of the bake-hardening index were explored under simulated paint bake conditions. Tensile properties were measured at selected temperatures between -100°C and 200°C and the TRIP effect was found to be temperature-dependent due to stress-induced martensitic transformation at lower temperatures versus strain-induced transformation at higher temperatures.